Low density oil fracturing proppant and preparation method thereof, and provides a shale gas fracturing proppant and preparation method, selection of raw materials according to weight including aluminum tailings 30~50, pyrojewel 25~40, 15, 1 alumina bauxite 10~20, which by crushing, mixing, grinding, heat the processing steps of processing to produce a product. The process is simple, easy to implement, to produce products with characteristics of low density, high strength, low acid solubility, suitable for fracturing shallow low permeability oil, natural gas and shale gas, can effectively improve the oil (gas) production wells and service life, full use of tailings resources, aluminum plant the waste, reduce pollution, change the market structure and current situation of domestic and foreign oil fracturing proppant.
【技术实现步骤摘要】
低密度石油压裂支撑剂及其制备方法
本专利技术属于石油化工领域，具体为一种页岩气的压裂支撑剂及其制备方法。
技术介绍
石油及天然气深井开采时，高闭合压力低渗透性矿床经压裂处理后，使含油气岩层裂开，油气从裂缝形成的通道中汇集而出，用支撑材料随同高压溶液进入地层充填在岩层裂缝中，起到支撑裂缝不因应力释放而闭合的作用，从而保持高导流能力，使油气畅通，增加产量。目前，国内石油压裂支撑剂厂家大多采用高品位的高铝矾土为主要原料生产的支撑剂产品，随着高铝矾土等不可再生资源的大幅减少，市场价格一路上涨，石油压裂支撑剂需要采用新的原料新的加工工艺，以满足人们对其的需求。
技术实现思路
本专利技术的目的在于提供一种低密度石油压裂支撑剂及其制备方法。为实现上述目的，本专利技术提出的技术方案为：低密度石油压裂支撑剂，其原料按照质量份数包括铝厂尾矿30~50份、焦宝石25~40份、氧化铝1-15份、铝矾土10~20份，基于此原料的低密度石油压裂支撑剂的制备方法，制备步骤为：①破碎：将各种原料分别进行破碎；②混料：将破碎后的各种原料进行混合；③磨粉：将混合均匀的物料粉碎、磨粉；④热加工：将粉料经成...
【技术保护点】
低密度石油压裂支撑剂及其制备方法，其特征在于，其原料按照质量份数包括铝厂尾矿30~50份、焦宝石25~40份、氧化铝1‑15份、铝矾土10~20份，基于此原料的低密度石油压裂支撑剂的制备方法，制备步骤为：①破碎：将各种原料分别进行破碎；②混料：将破碎后的各种原料进行混合；③磨粉：将混合均匀的物料粉碎、磨粉；④热加工：将粉料经成球机压制成球后，烘干、煅烧，然后冷却筛分即得成品。
【技术特征摘要】
1.低密度石油压裂支撑剂及其制备方法，其特征在于，其原料按照质量份数包括铝厂尾矿30~50份、焦宝石25~40份、氧化铝1-15份、铝矾土10~20份，基于此原料的低密度石油压裂支撑剂的制备方法，制备步骤为：①破碎：将各种原料分别进行破碎；②混料：将破碎后的各种原料进行混合；③磨粉：将混合均匀的物料粉碎、磨粉；④热加工：将粉料经成球机压制成球后，烘干、煅烧，然后冷却筛分即得成品。2.根据权利要求1所述的低密度石油压裂支撑剂及其制备方法，其特征在于，所述物料通过颚式破碎机进行粉碎，粉碎颗粒直径小于...