The invention relates to a sulfuric acid leaching liquid iron removal method comprises: A, adding H2O2 solution, H2O2 solution and sulfuric acid leaching solution volume ratio is 2%~2.5%; the quality of the concentration of H2O2 was 30%; two, adding sodium hydroxide solution; concentration of sodium hydroxide solution was 50%~ 60%; adjusting the pH value to 1.2~1.5 three, adding CaO solution; quality; the concentration of CaO was 5%~10%; the temperature is 90 to 95 DEG C; using 40~50min solution adjusted to pH=1.5; 40~50min will use the solution adjusted to pH=2.0; 40~50min will use the solution adjusted to pH=2.5; 40~50min will use the solution adjusted to pH=3.0; four, cooling, filtering to remove slag in addition, obtained after iron sulfate leaching solution. The iron content of the leaching solution of sulfuric acid after the addition of iron is less than 100mg/L.
【技术实现步骤摘要】
本专利技术涉及一种硫酸浸取液的除铁方法，特别是涉及一种产品中铀含量高，后期处理方便的硫酸浸取液的除铁方法。
技术介绍
从硫酸浸出液中加工浓缩提取铀，用得比较多的方法有离子交换吸附法和萃取法，两者具有选择性好，能得到铀含量很高的化学浓缩物，铀的回收率高，能减少酸耗、简化操作，因此在铀矿加工过程中广泛使用。此外，也有采用沉淀法，使铀从溶液中沉淀下来生成黄饼浓缩物，再进一步精制成核纯级铀化合物。但由于灰渣硫酸浸出液中铀含量高，杂质含量高，本文采用化学沉淀法对硫酸浸出液中的铀进行提取浓缩。从铀浸出液中用沉淀法回收铀最典型的方法是分步沉淀法：即用碱(苛性钠、氧化钙、氨水等)首先控制pH在3.5将铁沉淀；再将pH调到6.5～7.5沉淀铀。在这种工艺中，由于铁沉淀时的载带造成铀损失量大；且生成的沉淀是无定形的氢氧化铁，难以过滤和洗涤，而沉淀铀时仍有其它杂质如铝和少量钙等一起沉淀出来；沉淀产品的质量不高，往往需要进一步精制。在铀矿冶中也用过其它一些沉淀方法：如...
【技术保护点】
一种硫酸浸取液的除铁方法，依次包括以下步骤：第一步、使用H2O2溶液氧化Fe2+；H2O2溶液与硫酸浸取液的体积比为2%~2.5%；H2O2溶液的质量浓度为30%；第二步、加入氢氧化钠溶液；氢氧化钠溶液的质量浓度为50%~60%；调节pH值至1.2~1.5;第三步、加入CaO溶液；CaO溶液的质量浓度为5%~10%；温度为90～95℃；利用40~50min将溶液调节为pH=1.5；利用40~50min将溶液调节为pH=2.0；利用40~50min将溶液调节为pH=2.5；利用40~50min将溶液调节为pH=3.0；第四步、冷却至40℃~50℃，抽滤除去铁矾渣，得到除铁后的硫酸浸取液。
【技术特征摘要】
1.一种硫酸浸取液的除铁方法，依次包括以下步骤：
第一步、使用H2O2溶液氧化Fe2+；
H2O2溶液与硫酸浸取液的体积比为2%~2.5%；H2O2溶液的质量浓度为
30%；
第二步、加入氢氧化钠溶液；
氢氧化钠溶液的质量浓度为50%~60%；
调节pH值至1.2~1.5;
第三步、加入CaO溶液；
CaO溶...
【专利技术属性】
技术研发人员：孙自福，郭翔，
申请(专利权)人：中核建中核燃料元件有限公司，
类型：发明