The present invention relates to the use of lactide (LA) adhesive materials prepared by chemical synthesis products were biodegradable, LA material according to the solvent quality 5% 50% proportion, into the reaction container with the solvent in the reactor with stirring and temperature control function, control reactor under nitrogen gas protection, control at the same time, reaction temperature, stirring, LA completely melted, catalyst, reaction time, stop stirring, take out after centrifugation to obtain LA extraction, chemical synthesis products. Then, the chemical synthesis product of lactide (LA) was dissolved with ethyl acetate to obtain biodegradable adhesive. The adhesive has the advantages of simple preparation, molecular weight and viscosity controllable and biodegradable, can be used for leather, tape, stickers, stationery, office, electronic, automobile trim fixed, shoes, handmade jewelry stuck etc..
【技术实现步骤摘要】
一种可生物降解丙交酯低聚物胶粘剂及其制备方法和用途
本技术涉及化工材料领域，特别是一种利用丙交酯(LA)化学合成产物制备得到的可生物降解的胶粘剂材料及其制备方法。
技术介绍
目前，市场上胶黏剂的类型比较多，在胶带、文具、手工饰品等各种行业中都发挥了极其重大的作用。大多数产品虽然在初粘性、持粘性、剥离强度等方面符合要求，但在环保安全等方面却存在较大隐患。由于传统的胶粘剂在自然环境中很难降解，被应用于塑料、皮革、纸张等制品后，随这些制品被废弃后而进入环境，由于不能降解造成了“污染”，已成为自然环境保护的重大隐患，解决此方面问题逐渐成为当前研发的热点。近年来，少数研究人员开始研究可降解胶粘剂，例如，CN00128743.5报道了由聚天冬氨酸、其盐及其衍生物与天然增稠剂树脂的混合物制成的水溶性胶黏剂。虽然该专利中描述为可生物降解，但并没有具体说清楚混合物胶黏剂的生物降解率到底是多少。另外，水性胶黏剂的耐水性、耐溶剂性、胶膜强度等性能较差，且根据合成工艺分析，其成本也很高。总的来说，生产简单、易操作、成本低、可生物降解的胶粘剂的研制仍是很少见。
技术实现思路
本专利技术的目的是...
【技术保护点】
一种可生物降解胶粘剂及其制备方法，其特征在于该胶粘剂的成分为：丙交酯(LA)化学合成产物 10‑90份；溶剂 10‑90份。
【技术特征摘要】
1.一种可生物降解胶粘剂及其制备方法，其特征在于该胶粘剂的成分为：丙交酯(LA)化学合成产物10-90份；溶剂10-90份。2.根据权利要求1所述的生物降解胶粘剂，特征在于，黏度为50-5000mPa·S，剥离强度≥2.5(N/cm)，初粘力(球号)≥5，持粘力≥0.8h，相对生物分解率≥90％。3.根据权利要求1、2所述的丙交酯(LA)化学合成产物，其制备方法在于包括以下步骤：将LA材料按溶剂质量的5％-50％比例，倒入装有溶剂的反应容器中，反应器带搅拌与控温功能，控制反应器在氮气保护下，控制一定反应温度，同时进行搅拌，LA完全熔...
【专利技术属性】
技术研发人员：翁云宣，张明慧，张扬，
申请(专利权)人：北京工商大学，
类型：发明
国别省市：北京,11
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。