一种聚丙烯复合材料及其制备方法技术

本发明专利技术提供了一种聚丙烯复合材料及其制备方法。本发明专利技术得到的聚丙烯复合材料与现有的聚丙烯复合材料相比，除了表面光泽有所提高之外，溶体流动速率、弯曲强度和弯曲模量也均有所提高。具体的，由实施例的实验结果可知，本发明专利技术得到的聚丙烯复合材料的表面光泽度最高可提高18％，溶体流动速率最高可提高28g/10min，弯曲强度最高可提高2MPa，弯曲模量最高可提高300MPa。

Polypropylene composite material and preparation method thereof

The invention provides a polypropylene composite material and a preparation method thereof. Compared with the existing polypropylene composite material, the polypropylene composite material obtained by the invention has improved flow velocity, bending strength and bending modulus in addition to surface gloss. Specifically, the experimental results show the embodiment, the surface gloss polypropylene composite material obtained by the invention can improve the maximum solution 18%, the highest flow rate can be increased by 28g/10min, the maximum bending strength can be increased by 2MPa, the highest flexural modulus can be increased by 300MPa.

【技术实现步骤摘要】
一种聚丙烯复合材料及其制备方法
本专利技术涉及复合材料
，尤其涉及一种聚丙烯复合材料及其制备方法。
技术介绍
聚丙烯是一种用途广泛的通用塑料，由丙烯单体聚合而成，英文缩写为PP，其熔点为165～175℃，属半结晶性塑料。聚丙烯树脂根据聚合方法和分子链段排列形式，主要分为共聚、均聚两大类。由于普通聚丙烯树脂很难满足各种行业的应用要求，改性聚丙烯材料已经被应用的非常广泛。但随着如汽车、家电等行业对改性聚丙烯的技术水平要求日益提高，同时对材料的加工特性也提出一些更高的要求。如改性聚丙烯作为吸尘器外壳材料，既要具有良好的耐冲击性能，又要具有优异的外观，如高光泽等特点，此外还需具备一定的尺寸稳定性和加工特性。目前，虽然现有技术中的改性聚丙烯对材料的韧性有一定程度上的改善。但是，这些改性聚丙烯却普遍存在着光泽度差的缺点。
技术实现思路
本专利技术的目的在于提供一种聚丙烯复合材料及其制备方法，本专利技术提供的聚丙烯复合材料在保证材料的韧性的同时具有优异的光泽度。本专利技术提供了一种聚丙烯复合材料，由包含以下质量份的原料制备得到：优选的，所述均聚聚丙烯的熔融指数≥2g/10min。优选的，所述共聚本文档来自技高网...

【技术保护点】
一种聚丙烯复合材料，由包含以下质量份的原料制备得到：

【技术特征摘要】
1.一种聚丙烯复合材料，由包含以下质量份的原料制备得到：2.根据权利要求1所述的聚丙烯复合材料，其特征在于，所述均聚聚丙烯的熔融指数≥2g/10min。3.根据权利要求1所述的聚丙烯复合材料，其特征在于，所述共聚聚丙烯为高流动共聚聚丙烯和/或高结晶共聚聚丙烯；所述高流动共聚聚丙烯的熔融指数≥20g/10min；所述高结晶共聚聚丙烯的熔融指数≥8kg/10min。4.根据权利要求1～3任意一项所述的聚丙烯复合材料，其特征在于，所述增韧剂为乙烯与长直链烯烃的混合物；所述长直链烯烃为己烯或辛烯。5.根据权利要求1～3任意一项所述的聚丙烯复合材料，其特征在于，所述填料为超细硫酸钡。6.根据权利要求1～3任意一项所述的聚丙烯复合材料，其特征在于，所述成核剂为芳基磷酸酯盐。7.根据权利要求1～3任意一项所述的聚丙烯复合材料，其特征在于，所述主抗氧剂为四[β-(3，5-二特丁基4-羟基苯基)丙酸]季戊四醇酯；所述辅抗氧剂为三(2,4-二叔丁基酚...

【专利技术属性】
技术研发人员：李智，侯书征，
申请(专利权)人：吉林恒辉新材料有限公司，
类型：发明
国别省市：吉林,22