The invention discloses a low resistance composite electromagnetic shielding plastic, which comprises the following components: 60~80 weight portions, 10~30 black matrix resin, asphalt base chopped graphite fiber 10~20, surface treatment agent, toughening agent 5~10 copies of 20~30 copies, 3~8 copies of antioxidants. The invention relates to a low resistance composite electromagnetic shielding plastic, through the material science and the ratio of raw materials and surface treatment of filler material, effectively improve the frequency of electromagnetic shielding and mechanical properties of electromagnetic shielding plastic, and greatly reduces the low resistivity of the composite plastics, comprehensive performance, market prospects.
【技术实现步骤摘要】
一种低阻复合电磁屏蔽塑料
本专利技术涉及改性塑料
，特别是涉及一种低阻复合电磁屏蔽塑料。
技术介绍
电磁屏蔽塑料是导电塑料在电磁兼容领域的重要应用。现有电磁屏蔽塑料大都采用单一的导电填料制备而成，存在电阻大、耐腐蚀性差的缺陷，且在电磁屏蔽能效填料较多时，力学性能下降严重，不能满足使用要求。
技术实现思路
本专利技术主要解决的技术问题是提供一种低阻复合电磁屏蔽塑料。为解决上述技术问题，本专利技术采用的一个技术方案是：提供一种低阻复合电磁屏蔽塑料，包括如下重量份组分：基体树脂60～80份、炭黑10～30份、沥青基短切石墨纤维10～20份、表面处理剂5～10份、增韧改性剂20～30份、抗氧剂3～8份。在本专利技术一个较佳实施例中，所述基体树脂为聚丙烯、聚乙烯、丙烯腈-丁二烯-苯乙烯塑料、聚对苯二甲酸乙二醇酯，或是其中两种的混合物。在本专利技术一个较佳实施例中，所述表面处理剂为硅烷偶联剂或钛酸酯偶联剂。在本专利技术一个较佳实施例中，所述增韧改性剂为热塑性弹性体。在本专利技术一个较佳实施例中，所述沥青基短切石墨纤维为活性沥青基短切石墨纤维，其激活处理方法为：（1）氧化处理...
【技术保护点】
一种低阻复合电磁屏蔽塑料，其特征在于，包括如下重量份组分：基体树脂60～80份、炭黑10～30份、沥青基短切石墨纤维10～20份、表面处理剂5～10份、增韧改性剂20～30份、抗氧剂3～8份。
【技术特征摘要】
1.一种低阻复合电磁屏蔽塑料，其特征在于，包括如下重量份组分：基体树脂60～80份、炭黑10～30份、沥青基短切石墨纤维10～20份、表面处理剂5～10份、增韧改性剂20～30份、抗氧剂3～8份。2.根据权利要求1所述的低阻复合电磁屏蔽塑料，其特征在于，所述基体树脂为聚丙烯、聚乙烯、丙烯腈-丁二烯-苯乙烯塑料、聚对苯二甲酸乙二醇酯，或是其中两种的混合物。3.根据权利要求1所述的低阻复合电磁屏蔽塑料，其特征在于，所述表面处理剂为硅烷偶联剂或钛酸酯偶联剂。4.根据权利要求1所述的低阻复合电磁屏蔽塑料，其特征在于，所述增韧改性剂为热塑性弹性体。5.根据权利要求1所述的低阻复合电磁屏蔽塑料，其特征在于，所述沥青基短切石墨纤维为活性沥青基短切石墨纤维，其活化处理方法为...