The invention discloses a high hydrophobic scratch resistant polypropylene material and a preparation method thereof. A high hydrophobic scratch resistant polypropylene material, according to the mass fraction comprises the following components: PP resin 65 ~ 85%, 8 ~ 17% barium sulfate and fluoride additives from 2 to 15%, Zinc Oxide 2 ~ 8%, 2 ~ 8% silicone masterbatch, antioxidant 0.2 ~ 0.6% and 0.3 ~ 0.7% lubricant. A method for preparing high hydrophobic scratch resistant polypropylene material is also disclosed. The polypropylene material of the invention has the characteristics of high hydrophobicity and scratch resistance, and solves the problem that the inner wall of the dishwasher is easy to hang water and is not scratch resistant.
【技术实现步骤摘要】
一种高疏水性耐刮擦聚丙烯材料及其制备方法
本专利技术涉及一种高疏水性耐刮擦聚丙烯材料及其制备方法。
技术介绍
聚丙烯由于具有无毒、无味、成本低、机械性能好等特点在家电、电子等领域具有广泛的应用。例如洗碗机内胆、刀叉篮等都是聚丙烯改性材料。但是，聚丙烯在洗碗机的应用中存在一个问题，洗碗机使用烘干之后，洗碗机内胆、刀叉篮等内壁会冷凝许多水珠，容易滴落而污染到餐具上，这严重影响消费者的使用体验；且聚丙烯不耐刮擦，使用一段时间后容易出现或深或浅的刮痕，从而容易使脏污残留其中。因而，提高聚丙烯的疏水性能，减少洗碗机挂水珠，提高材料的耐刮擦具有重要意义。在化学里，疏水性指的是一个分子(疏水物)与水互相排斥的物理性质，一般用水接触角来表征。一般地，水接触角小于90°标示亲水性好(疏水性差)，水接触角大于110°表示具有高疏水性，水接触角大于150°表示具有超疏水性(如荷叶)。决定表面疏水性能的主要因素主要有两个：一是表面微结构或者粗糙度，只有表面微结构由纳米或者微米-纳米复合结构组成才有可能制造出超疏水表面；第二是表面自由能，只有低的表面能组成的化学材料才有可能构造出超疏水表面...
【技术保护点】
一种高疏水性耐刮擦聚丙烯材料，其特征在于：按质量分数包括以下组分：PP树脂 65～85％；硫酸钡 8～17％；含氟助剂 2～15％；氧化锌 2～8％；硅酮母粒 2～8％；抗氧剂 0.2～0.6％；润滑剂 0.3～0.7％。
【技术特征摘要】
1.一种高疏水性耐刮擦聚丙烯材料，其特征在于：按质量分数包括以下组分：PP树脂65～85％；硫酸钡8～17％；含氟助剂2～15％；氧化锌2～8％；硅酮母粒2～8％；抗氧剂0.2～0.6％；润滑剂0.3～0.7％。2.根据权利要求1所述的一种高疏水性耐刮擦聚丙烯材料，其特征在于：PP树脂为均聚PP和共聚PP按质量比(5～3)：1组成的复配物。3.根据权利要求1所述的一种高疏水性耐刮擦聚丙烯材料，其特征在于：硫酸钡为纳米级沉淀硫酸钡。4.根据权利要求1所述的一种高疏水性耐刮擦聚丙烯材料，其特征在于：含氟助剂为全氟烷烃、含氟有机硅中的至少一种。5.根据权利要求1所述的一种高疏水性耐刮擦聚丙烯材料，其特征在于：氧化锌为纳米级氧化锌。6.根据权利要求1所述的一种高疏水性耐刮擦聚丙烯材料，其特征在于：硅酮母粒的硅酮含...
【专利技术属性】
技术研发人员：于海鸥，杨华军，王灿耀，易庆锋，何继辉，方安平，
申请(专利权)人：广东圆融新材料有限公司，
类型：发明
国别省市：广东,44