The invention discloses a hydrophilic modification method of waste tire powder based on mortar fluidity, the waste tire rubber powder by low-temperature plasma activation, alkali solution modified by TEOS as silicon source, forming a layer of inorganic SiO2 network in the scrap rubber powder surface by sol gel method so as to improve the. Hydrophilic rubber powder. The invention of modified rubber powder wetting contact angle with water significantly reduced, rubber powder can significantly improve the hydrophilicity, binding force and conducive to building mortar interface, generate more connection with the surface of the water molecule in mortar particles, water film formed more stable, which favors the sliding of particles, so that the fluidity of cement base composite material increase.
【技术实现步骤摘要】
一种基于砂浆流动性对废旧轮胎胶粉进行亲水改性的方法
本专利技术涉及废旧轮胎胶粉的再利用
，具体涉及一种基于砂浆流动性对废旧轮胎胶粉进行亲水改性的方法。
技术介绍
随着汽车工业的迅速发展，废弃轮胎的排量急剧增加，废弃轮胎造成的环境污染已成为世界性问题之一。由于大量废弃轮胎堆放挤占土地，对自然环境造成破坏，因此废弃轮胎的再利用是急需解决的问题。我国2010年废弃轮胎达到2亿条，但每年废弃轮胎的处理量只有14%左右，必须为废弃轮胎胶粉寻找一条安全、大量消化的途径。橡胶混凝土使废旧轮胎得到了再利用、减少传统处理方式造成的排碳量过大的污染，同时改善了混凝土的弹塑性、韧性等性能，近年来得到了广泛学者专家的研究关注。然而，由于橡胶粉表面凹凸不平容易吸附水分，导致橡胶粉亲水性降低，使得水泥和标准砂的黏结性降低，从而对混凝土的工作性能以及其他各种性能造成不利的影响。
技术实现思路
本专利技术提供了一种基于砂浆流动性对废旧轮胎胶粉进行亲水改性的方法，增强胶粉的亲水性，从而达到提高水泥基胶凝材料的流动性能的目的。一种基于砂浆流动性对废旧轮胎胶粉进行亲水改性的方法，将废旧轮胎胶粉进行低...
【技术保护点】
一种基于砂浆流动性对废旧轮胎胶粉进行亲水改性的方法，其特征在于，将废旧轮胎胶粉进行低温等离子体活化，碱溶液浸泡改性，之后以正硅酸乙酯为硅源，采用溶胶‑凝胶法在废胶粉表面形成一层SiO2无机网络，从而提高胶粉的亲水性。
【技术特征摘要】
1.一种基于砂浆流动性对废旧轮胎胶粉进行亲水改性的方法，其特征在于，将废旧轮胎胶粉进行低温等离子体活化，碱溶液浸泡改性，之后以正硅酸乙酯为硅源，采用溶胶-凝胶法在废胶粉表面形成一层SiO2无机网络，从而提高胶粉的亲水性。2.根据权利要求书1所述的一种基于砂浆流动性对废旧轮胎胶粉进行亲水改性的方法，其特征在于，具体步骤如下：（1）低温等离子体活化：将80-100重量份废旧轮胎胶粉均匀平铺在100目筛网上，水平放置于低温等离子体活化仪内腔中，抽真空至腔内气压真空度为30-60Pa，开启电源放电，控制腔内气压满足辉光放电，产生低温等离子体，活化2-8分钟；（2）碱洗：将强碱氢氧化钠颗粒加入去离子水中，配置成浓度为5%的氢氧化钠溶液，加入上述活化处理后的胶粉，强力搅拌混合后，浸泡20-50分钟后，用清水清洗至中性后，放入65-8...
【专利技术属性】
技术研发人员：李国友，
申请(专利权)人：安徽中宏橡塑有限公司，
类型：发明
国别省市：安徽,34