一种以爆发成核法制备壳聚糖微球的方法技术
Method for preparing chitosan microsphere by explosive nucleation method
The invention discloses a method for preparing chitosan microspheres by the explosive nucleation process, is adding 0.1 ~ 0.4mol/L of chitosan in acetic acid aqueous solution, the concentration of chitosan is 1 ~ 2wt%, prepared chitosan solution, uniform and transparent, and the solution of Moore added urea, then put into the reaction kettle in 60 ~ 160 DEG C under heating, the reaction time is 2 ~ 8h, to obtain chitosan microspheres. The synthetic process and equipment of the invention are simple, and the chitosan microsphere has uniform particle size, low cost, high efficiency, environmental protection, short reaction cycle, good repeatability and wide industrial application prospect.
【技术实现步骤摘要】
一种以爆发成核法制备壳聚糖微球的方法
本专利技术涉及一种制备壳聚糖微球的方法，尤其涉及一种以壳聚糖为主要原料，醋酸、尿素等无毒试剂为辅助原料，以爆发成核法制备壳聚糖微球的方法；属于高分子生物材料及其制备领域。
技术介绍
壳聚糖(英语：Chitosan)，是一种线性多糖，当中由氨基葡萄糖(脱乙酰单位)和N-乙酰葡糖胺(乙酰单位)随机分布，并透过β-(1-4)糖苷键组合而成。是由自然界广泛存在的几丁质(chitin)经过脱乙酰作用得到的，化学名称为聚葡萄糖胺(1-4)-2-氨基-B-D葡萄糖。它在商业和生物医学用途广泛，在医药、食品、化工、化妆品、水处理、金属提取及回收、生化和生物医学工程等诸多领域的应用研究取得了重大进展。尤其是在生物医学方面具有良好的生物相容性、无生物毒性，是当作生医材料的骨架非常好的选择。目前关于壳聚糖微球载药性能的研究，已经有不同的探索和成果，但具有市场潜力的大多成果尚处于研究阶段。因此壳聚糖微球的制备研究已经成为目前的一个研究热点，目前就国内外壳聚糖微球的制备方法，主要有交联法、凝聚法、乳化溶剂蒸发法，壳聚糖微球溶液包液法、壳聚糖微球乙酰化法...
【技术保护点】
一种以爆发成核法制备壳聚糖微球的方法，步骤是：①壳聚糖溶液配制：将壳聚糖加入0.1～0.4mol/L醋酸水溶液中，使壳聚糖质量分数为1～2wt％，在室温下搅拌至壳聚糖完全溶解，经超声除气，制得均匀透明的壳聚糖溶液，标记为A溶液；其中，所述壳聚糖的脱乙酰度≥80％，壳聚糖粘度为低粘度即<200mPa·s，或中粘度即200‑400mPa·s，或高粘度即>400mPa·s；②取设定体积的A溶液，并以A溶液中所含醋酸物质的量按尿素与醋酸的摩尔比为5:1～1:5的比例加入尿素，超声除气，所得溶液标记为B溶液；③将制得的B溶液倒入配有搅拌功能的聚四氟乙烯的高温高压反应釜中，...
【技术特征摘要】
1.一种以爆发成核法制备壳聚糖微球的方法，步骤是：①壳聚糖溶液配制：将壳聚糖加入0.1～0.4mol/L醋酸水溶液中，使壳聚糖质量分数为1～2wt％，在室温下搅拌至壳聚糖完全溶解，经超声除气，制得均匀透明的壳聚糖溶液，标记为A溶液；其中，所述壳聚糖的脱乙酰度≥80％，壳聚糖粘度为低粘度即<200mPa·s，或中粘度即200-400mPa·s，或高粘度即>400mPa·s；②取设定体积的A溶液，并以A溶液中所含醋酸物质的量按尿素与醋酸的摩尔比为5:1～1:5的比例加入尿素，超声除气，所得溶液标记为B溶液；③将制得的B溶液倒入配有搅拌功能的聚四氟乙烯的高温高压反应釜中，控制填充率为50％～80...
【专利技术属性】
技术研发人员：李海东，唐建国，黄林军，王彦欣，
申请(专利权)人：青岛大学，
类型：发明
国别省市：山东,37