An antibacterial porcelain of the present invention, is characterized by including the ceramic body, the ceramic body is arranged on the surface of antibacterial glaze layer, the antibacterial glaze layer comprises the following raw materials in parts by weight: 20 calcined kaolin 34; nano titanium dioxide: 1 4; Al18B4O33: 2 6; aluminum phosphate: 2 7; 0.5 3: tungsten oxide; zirconia 2.5: 5; 5: 3 lead carbonate; quartz sand: 5 10. The invention provides an antibacterial porcelain, nanometer TiO2 as antibacterial material is added to the antibacterial glaze layer, made out of porcelain itself has the appearance at the same time, also has a bactericidal and bacteriostatic effect on Staphylococcus aureus killing rate of 95%, increased health and safety in the process of using, and preparation the method is simple, and is suitable for industrial production.
【技术实现步骤摘要】
一种抗菌瓷器及其制备工艺
本专利技术涉及一种抗菌瓷器及其制备工艺。
技术介绍
关于抗菌釉及其加工方法，提出有各种方案。通常银系无机抗菌剂由于具有优异的耐热性，所以现在有很多将其用作抗菌釉的研究。但是，虽说是银系无机抗菌剂，但大多数情况下是通过配合在釉中且涂布到陶瓷器的表面后，在超过1000℃的高温下进行烧成，由此利用银系无机抗菌剂的分解、熔解以及挥发等使抗菌效力明显降低。因此，需要一种提高抗菌效力的抗菌瓷器。
技术实现思路
为解决上述存在的问题，本专利技术的目的在于提供一种抗菌瓷器。所述抗菌瓷器，将纳米二氧化钛作为抗菌材料加入到抗菌釉层，所烧制出的瓷器本身具有美观的同时，还具有抑菌杀菌的作用，对金黄色葡萄球菌的抑杀率可达95%，增加了使用过程中的卫生安全性，且制备方法简单，有利于工业化生产。为达到上述目的，本专利技术的技术方案是：一种抗菌瓷器，包括陶瓷胚体，所述陶瓷胚体表面设置有抗菌釉层，所述抗菌釉层包括如下重量份数的原料：煅烧高岭土：20-34份；纳米二氧化钛：1-4份；硼酸铝：2-6份；偏磷酸铝：2-7份；氧化钨：0.5-3份；氧化锆：2.5-5份；碳酸铅：3-5...
【技术保护点】
一种抗菌瓷器，其特征在于，包括陶瓷胚体，所述陶瓷胚体表面设置有抗菌釉层，所述抗菌釉层包括如下重量份数的原料：煅烧高岭土：20‑34份；纳米二氧化钛：1‑4份；硼酸铝：2‑6份；偏磷酸铝：2‑7份；氧化钨：0.5‑3份；氧化锆：2.5‑5份；碳酸铅：3‑5份；石英砂：5‑10份。
【技术特征摘要】
1.一种抗菌瓷器，其特征在于，包括陶瓷胚体，所述陶瓷胚体表面设置有抗菌釉层，所述抗菌釉层包括如下重量份数的原料：煅烧高岭土：20-34份；纳米二氧化钛：1-4份；硼酸铝：2-6份；偏磷酸铝：2-7份；氧化钨：0.5-3份；氧化锆：2.5-5份；碳酸铅：3-5份；石英砂：5-10份。2.根据权利要求1所述的一种抗菌瓷器，其特征在于，所述抗菌釉层包括如下重量份数的原料：煅烧高岭土：20-28份；纳米二氧化钛：2-4份；硼酸铝：2-5份；偏磷酸铝：4-7份；氧化钨：1.5-3份；氧化锆：2.5-3.5份；碳酸铅：4-5份；石英砂：7-10份。3.根据权利要求1所述的一种抗菌瓷器，其特征在于，所述抗菌釉层包括如下重量份数的原料：煅烧高岭土：25份；纳米二氧化钛：3份；硼酸铝：3份；偏磷酸铝：6份；氧化钨：2...