The invention provides a high temperature binder for ceramic glaze sticker printing, involving bonding materials, by weight of raw materials prepared by the 30 50 quartz and feldspar, kaolin 30 20 5 15 copies, 15 copies, 5 borax dextrin 1 10 polyacrylamide, 10 20, 0.5 phosphate 1.5 copies, 5 copies, 1 zirconia alumina 1 5, 1 5 silica fume and water 70 100 copies, the preparation method comprises: weighing materials, quartz, feldspar and borax will melt mixing and crushing cooling, crushing and sieving, wet milling and addition of kaolin cyclodextrin and polyacrylamide and finally add water, phosphoric acid, zirconium oxide, alumina and silica fume, heating and stirring, cooling, can get the finished product, the invention has the advantages of good adhesive effect, high strength, good stability, high temperature resistance.
【技术实现步骤摘要】
一种陶瓷釉中彩贴纸印花用高温粘结剂
本专利技术涉及粘结材料领域，具体涉及一种陶瓷釉中彩贴纸印花用高温粘结剂。
技术介绍
七十年代发展起来的一种新的瓷器装饰材料和技法。亦称高温快烧颜料。颜料的熔剂成分不含铅或少含铅，按釉上彩方法施于器物釉面，通过高温快烧，釉面软化熔融，使颜料渗入釉内，冷却后釉面封闭。细腻晶莹、滋润恍目，抗腐蚀、耐磨损，具有釉下彩的效果，其中釉中贴花是其中的重要一步，具体操作是一次上釉素烧后利用粘结剂贴花，再上釉进行二次釉烧，二次釉烧温度高，约为1300-1400℃之间，高温会使粘结剂硬化，粘度降低，进而导致陶瓷成品花纹失真、重叠、移位等，造成经济损失。国外市场上，陶瓷型高温粘结剂的研究十分活跃，国外也有企业开始生产，但是配方却很少发表，比如曼尔派尔公司生产的CA-110粘结剂的接头耐温达到1400℃，目前国内这方面的研究虽然才刚刚起步，但是已经卓有成效。
技术实现思路
(一)解决的技术问题针对现有技术的不足，本专利技术提供了一种陶瓷釉中彩贴纸印花用高温粘结剂，具有强度高、稳定性好、耐高温的优点。(二)技术方案为实现以上目的，本专利技术通过以下技术方案予...
【技术保护点】
一种陶瓷釉中彩贴纸印花用高温粘结剂，其特征在于，由以下重量份的原料制备而成：石英30‑50份、长石20‑30份、高岭土5‑15份、硼砂5‑15份、糊精1‑10份、聚丙烯酰胺10‑20份、磷酸0.5‑1.5份、氧化锆1‑5份、氧化铝1‑5份、硅粉1‑5份、水70‑100份。
【技术特征摘要】
1.一种陶瓷釉中彩贴纸印花用高温粘结剂，其特征在于，由以下重量份的原料制备而成：石英30-50份、长石20-30份、高岭土5-15份、硼砂5-15份、糊精1-10份、聚丙烯酰胺10-20份、磷酸0.5-1.5份、氧化锆1-5份、氧化铝1-5份、硅粉1-5份、水70-100份。2.如权利要求1所述的陶瓷釉中彩贴纸印花用高温粘结剂，其特征在于，由以下重量份的原料制备而成：石英35-45份、长石24-28份、高岭土7-12份、硼砂7-12份、糊精3-7份、聚丙烯酰胺12-16份、磷酸0.7-1.2份、氧化锆2-4份、氧化铝2-4份、硅粉2-4份、水80-90份。3.如权利要求1或2所述的陶瓷釉中彩贴纸印花用高温粘结剂，其特征在于，其制备方法包括以下步骤：(1)按比例称取所需物料；(2)将石...
【专利技术属性】
技术研发人员：裴仕林，
申请(专利权)人：安徽青花坊瓷业股份有限公司，
类型：发明
国别省市：安徽,34