Anti glare treatment method of cover plate, anti glare cover plate and display device
The invention discloses an anti glare treatment method for a cover plate, an anti glare cover plate and a display panel. The method includes: a layer of micron sized inorganic particles formed on the surface of a cover plate; forming a layer of organic matter in micron inorganic particles; to cover high temperature rolling processing, the organic melting in viscous flow; after high temperature treatment on the cover of rolling cooling treatment, the inorganic particles formed by the solidification of organic matter membrane dispersion is fixed on a cover plate. Based on this, the invention can ensure the anti glare effect, simplify the manufacturing process and reduce the cost.
【技术实现步骤摘要】
盖板的抗眩目处理方法、抗眩目盖板及显示装置
本专利技术涉及光学与显示
，具体涉及一种盖板的抗眩目处理方法、抗眩目盖板及显示面板。
技术介绍
随着科技的发展和社会的进步，手机已广泛应用于人们的日常生活中。为了避免用户在高亮度环境中观看手机屏幕时受到强光或者鬼影的干扰，业界通常对手机盖板的表面进行抗眩目处理，目前常用的盖板的抗眩目处理方法包括蚀刻法和喷涂法。但是，蚀刻法需要配置适当的酸液，不仅工艺繁琐，而且为了避免蚀刻废液污染环境，还需要对蚀刻废液进行处理，这使得制造成本居高不下，而采用喷涂法形成于盖板上的颗粒附着力不强，易脱落，抗眩目效果较差。
技术实现思路
有鉴于此，本专利技术提供一种盖板的抗眩目处理方法、抗眩目盖板及显示面板，能够确保抗眩目效果，简化制造工艺，降低成本。本专利技术一实施例的盖板的抗眩目处理方法，包括：在盖板的表面形成一层微米级无机颗粒；在无机颗粒上形成一层有机物；对盖板进行高温辊压处理，使得有机物熔融呈粘流态；对经过高温辊压处理的盖板进行冷却处理，使得无机颗粒被有机物固化形成的膜分散固定于盖板上。本专利技术一实施例的抗眩目盖板，包括基材以及覆盖...
【技术保护点】
一种盖板的抗眩目处理方法，其特征在于，所述方法包括：在盖板的表面形成一层微米级无机颗粒；在所述无机颗粒上形成一层有机物；对所述盖板进行高温辊压处理，使得所述有机物熔融呈粘流态；对经过所述高温辊压处理的盖板进行冷却处理，使得所述无机颗粒被有机物固化形成的膜分散固定于所述盖板上。
【技术特征摘要】
1.一种盖板的抗眩目处理方法，其特征在于，所述方法包括：在盖板的表面形成一层微米级无机颗粒；在所述无机颗粒上形成一层有机物；对所述盖板进行高温辊压处理，使得所述有机物熔融呈粘流态；对经过所述高温辊压处理的盖板进行冷却处理，使得所述无机颗粒被有机物固化形成的膜分散固定于所述盖板上。2.根据权利要求1所述的方法，其特征在于，所述有机物的制造材料的折射率和所述无机颗粒的制造材料的折射率相等。3.根据权利要求1所述的方法，其特征在于，所述无机颗粒的制造材料包括玻璃纤维、氧化铝Al2O3中的至少一种。4.根据权利要求1所述的方法，其特征在于，所述有机物的制造材料包括聚乙烯、聚甲基丙烯酸甲酯PMMA中的至少一种。5.根据权利要求1所述的方法，其特征在于，在盖板的表面形成一层微米级无机颗粒之前，所述方...