The invention discloses a DC transmission for polymerization of silicon insulator material and its preparation method and the application of the polymeric materials including silicon insulator phenolic latex, silicone, polyethylene, polypropylene and UV absorber. The composite silicon insulator used for DC transmission is used for making DC transmission insulators. The polymerization of silicon insulator materials made of insulator, which can meet the electrical characteristics of insulators, the traditional mechanical properties can meet the requirements of life, and can solve under DC voltage erosion problems, the problem of aging umbrella material with self-cleaning function, its high price ratio, energy saving and environmental protection, no pollution, products arrive after lifetime Recyclable reuse.
【技术实现步骤摘要】
直流输电用聚合晶硅绝缘子材料及其制备方法和应用
本专利技术属于绝缘子
，具体涉及一种直流输电用聚合晶硅绝缘子材料及其制备方法和应用。
技术介绍
随着经济的发展，我国的用电需求不断增加，又由于我国一次资源的分布极度不均匀，电力能源主要分布在西南部和西部地区，而电力需求相对集中在经济发展较好的东部、南部和中部地区，这导致能源的分布与需求存在不一致性，也使得远距离大容量的输电成为必然。直流输电是目前世界上电力大国解决远距离、大容量、高电压及电网互联的一个非常重要的手段。直流输电发展可分为四个阶段：20世纪以前的初级阶段；20世纪30年代至50年代的研究阶段；1954年至1970年的复兴阶段和1970年以后的迅速发展阶段。近些年来我国直流输电技术快速发展，直流线路的投运数量急剧增加。直流输电的发展对绝缘子的要求也提出了新的要求。由于直流电与交流电特性上的差异，对绝缘子的要求也逐步提高，例如直流线路的静电吸附作用，使其污秽能力要比同样条件下的交流线路的高，那么对直流线路绝缘子的抗污秽性能也就要求更高。传统的瓷绝缘子存在着诸多不足：1)、在制造传统的瓷绝缘子时，传统窑炉...
【技术保护点】
直流输电用聚合晶硅绝缘子材料，其特征在于，该聚合金硅绝缘子材料的原料包括酚醛胶乳、硅酮、聚乙烯、聚丙烯和紫外光吸收剂，按质量分数计算，聚乙烯占65％‑80％、聚丙烯占15％‑30％、硅酮占3％‑8％、酚醛胶乳占0.2％‑0.8％、紫外光吸收剂占0.3％‑0.6％。
【技术特征摘要】
1.直流输电用聚合晶硅绝缘子材料，其特征在于，该聚合金硅绝缘子材料的原料包括酚醛胶乳、硅酮、聚乙烯、聚丙烯和紫外光吸收剂，按质量分数计算，聚乙烯占65％-80％、聚丙烯占15％-30％、硅酮占3％-8％、酚醛胶乳占0.2％-0.8％、紫外光吸收剂占0.3％-0.6％。2.根据权利要求1的直流输电用聚合晶硅绝缘子材料，其特征在于，所述聚丙烯、聚乙烯的重均分子量均为10万～20万，硅酮的重均分子量为1000-1500。3.根据权利要求1的直流输电用聚合晶硅绝缘子材料，其特征在于，所述紫外光吸收剂为水杨酸苯脂、UV-P或UV-531中的一种。4.权利要求1-3所述的直流输电用聚合晶硅绝缘子材料的制备方法，其特征在于，包括如下步骤：步骤一、将天然乳胶加水稀释至量比为60％后倒入熟成酚醛树脂液中，并搅拌均匀，然后在室温下静置12小时，制得酚醛胶乳，其中胶乳与酚醛树脂液的质量比为1～...
【专利技术属性】
技术研发人员：严维逊，严姗芝，吴剑峰，
申请(专利权)人：江苏金三力电力器材实业有限公司，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。