The invention relates to a nanometer Zinc Oxide / Ag composite antibacterial agent and its preparation method, first of all to nano Zinc Oxide, silane coupling agent KH 560 as raw materials, preparation of epoxy nano Zinc Oxide; after using silver nitrate, epoxy nano Zinc Oxide and sodium citrate as raw material, through the preparation of nano composite antibacterial agent by Zinc Oxide Ag chemical reduction. The Zinc Oxide / silver nano antibacterial composite antibacterial agent applied to cotton fabric by ZnO and Ag, synergistic antibacterial, improve the efficiency of broad-spectrum antibacterial agent; through epoxy cotton fabric and the surface of nano ZnO surface hydroxyl can wash resistance can improve the antibacterial crosslinked cotton fabric; the preparation method is simple simple, low cost, environmentally friendly and harmless preparation process.
【技术实现步骤摘要】
纳米氧化锌/银复合抗菌剂及其制备方法
本专利技术涉及一种棉织物抗菌剂，具体涉及一种纳米氧化锌/银复合抗菌剂及其制备方法。
技术介绍
纺织品因其具有良好的舒适度和美观度，深受人们喜爱，在市场上拥有广大的需求，但是纺织品的多孔状是多种微生物和细菌霉菌生长的良好载体，它们不仅会污染纺织品，影响纺织品的质量，使纺织品变色或者发霉等等，而且这些细菌霉菌也会通过纺织品的传递影响到人体的健康，因此，日用和医用纺织品对抗菌剂有巨大的需求。纳米ZnO具有价格低廉、表面效应、小尺寸效应、量子效应和宏观量子隧道效应，展现出许多特殊的优异性能，如无毒、非迁移性、抗菌除臭、吸收和散射紫外线并且具备一定的抗菌性能，所以纳米ZnO成为开发功能绿色抗菌纺织品的重要材料之一。若将其直接应用于织物的抗菌整理中，存在耐水洗性差，对于霉菌抗菌效果不理想等缺点。纳米银及其化合物是一种广谱杀菌材料，杀菌能力较强，近年来，一些研究者采用金属银对氧化锌进行修饰，改变氧化锌的形貌，增大其催化面积，提高复合材料的光催化效率，实现广谱高效的抗菌性能。
技术实现思路
本专利技术的目的是提供一种纳米氧化锌/银复合抗菌剂及其制...
【技术保护点】
纳米氧化锌/银复合抗菌剂的制备方法，其特征在于：由以下步骤实现：步骤一：以纳米氧化锌、硅烷偶联剂KH‑560为原料，制备环氧基化纳米氧化锌；步骤二：以硝酸银、环氧基化纳米氧化锌、柠檬酸钠为原料，通过化学还原法制备纳米氧化锌/银复合抗菌剂。
【技术特征摘要】
1.纳米氧化锌/银复合抗菌剂的制备方法，其特征在于：由以下步骤实现：步骤一：以纳米氧化锌、硅烷偶联剂KH-560为原料，制备环氧基化纳米氧化锌；步骤二：以硝酸银、环氧基化纳米氧化锌、柠檬酸钠为原料，通过化学还原法制备纳米氧化锌/银复合抗菌剂。2.根据权利要求1所述的纳米氧化锌/银复合抗菌剂的制备方法，其特征在于：步骤一的具体步骤为：（1）将1.000质量份的纳米氧化锌溶解于30.000质量份的去离子水中，超声10min得到纳米氧化锌水溶液；（2）将0.010-0.030质量份的KH-560溶于20质量份的去离子水和2质量份的乙醇的混合液中，预水解1h得到KH-560水溶液；（3）将超声得到的纳米氧化锌溶液加入到250mL的三口烧瓶中，在30rpm的搅拌速度下，水温85℃反应，随后将预水解的KH-560水溶液在30min...
【专利技术属性】
技术研发人员：高党鸽，刘静静，李亚娟，吕斌，马建中，
申请(专利权)人：陕西科技大学，
类型：发明
国别省市：陕西,61