一种用于制备低成本耐高温钎焊铝/钢复合带材的铝合金及制备方法技术
Aluminum alloy for preparing low cost and high temperature resistant brazing aluminium / steel composite strip and preparation method thereof
The invention relates to an aluminum alloy used for preparing a low cost and high temperature resistant brazing aluminum / steel composite strip and a preparation method thereof, belonging to the technical field of alloy materials. The aluminum alloy used in the preparation of the high-temperature resistant brazing aluminum / steel composite belt has an Si content of 0.47% to 1.08wt.%, and the content of element Fe can reach up to 0.42 to 0.51wt.%. The aluminum / steel composite strip produced by aluminum alloy can effectively restrain the formation of interface compound during high temperature brazing. Thus, it can reduce the production cost by more than 4% while ensuring the high temperature brazing property of the aluminum / steel composite strip.
【技术实现步骤摘要】
一种用于制备低成本耐高温钎焊铝/钢复合带材的铝合金及制备方法
本专利技术涉及一种用于制备低成本耐高温钎焊铝/钢复合带材的铝合金，属于合金材料
技术背景铝/钢层状金属复合材料由于综合了钢的高强度、韧性、耐磨性以及铝良好的导热、导电、低密度等优异性能，已经在航空航天、机械、汽车、轮船、建筑以及电力和电子等领域得到了应用。其中，在电力领域，铝/钢复合带是生产火力发电空冷系统散热片的关键材料。铝/钢复合带是由铝板和钢板通过轧制复合+扩散退火的方法生产而成。铝侧合金传统上选用的多是1050铝合金，但是采用1050铝合金生产的铝/钢复合带在高温钎焊时界面容易产生硬脆的Fe-Al系金属间化合物，导致界面发生开裂，这被称为铝/钢复合带的“高温热脆性”。铝/钢复合带的“高温热脆性”问题限制了铝/钢复合带的广泛应用。大量研究表明，将适量的合金元素Si加入铝中制成的铝/钢复合带可以解决硬脆的Fe-Al系金属间化合物的产生。专利CN102321834A及专利CN104962789A中，分别通过在高纯铝中添加0.7-0.9wt.％及0.41-0.63wt.％的Si有效的抑制了铝...
【技术保护点】
一种用于制备低成本耐高温钎焊铝/钢复合带材的铝合金，其中钢为08Al钢，其特征在于，铝合金中Si的质量百分数为0～1.08wt.％，元素Fe的质量百分数为0～0.51wt.％，余量为铝及不可避免的其它杂质。
【技术特征摘要】
1.一种用于制备低成本耐高温钎焊铝/钢复合带材的铝合金，其中钢为08Al钢，其特征在于，铝合金中Si的质量百分数为0～1.08wt.％，元素Fe的质量百分数为0～0.51wt.％，余量为铝及不可避免的其它杂质。2.根据权利要求1所述的一种用于制备低成本耐高温钎焊铝/钢复合带材的铝合金，其特征在于，该合金中Si含量的成分范围为0.47％～1.08wt.％,元素Fe的含量最多可达到0.42～0.51wt.％。3.制备权利要求1或2所述的一种用于制备低成本耐高温钎焊铝/钢复合带材的铝合金的方法，其特征在于，在熔炼温度为790±10℃下，先将铝锭熔化，随后加入Al-Si中间合金，待中间合金熔化...