PVC专用强化剂制造技术

本发明专利技术公开了一种PVC专用强化剂，包含有棉花纤维、氧化聚乙烯蜡和聚氯乙烯，其质量份数配比如下：棉花纤维10％‑22％；氧化聚乙烯蜡4&‑8％；聚氯乙烯70％‑86％；该强化剂的制作工艺步骤如下：(1).利用氧化聚乙烯蜡对棉花纤维进行包膜；(2).将包膜后的棉花纤维与PVC进行物理链接；本发明专利技术通过提供一种包含有棉花纤维、氧化聚乙烯蜡和聚氯乙烯PVC专用强化剂，并结合本发明专利技术提供的制作工艺，达到强化制品强度和保证产品质量的目的。

PVC special fortifier

The present invention discloses a kind of special agent PVC, including cotton fiber, oxidized polyethylene wax and polyvinyl chloride, the mass fraction ratio is as follows: 10% cotton fiber 22%; opew 4& 8%; 70% PVC 86%; the fortifier manufacturing process steps are as follows: (1) were coated on cotton. The use of fiber oxidized polyethylene wax; (2). The cotton fiber and PVC coated by physical links; the present invention provides a cotton fiber, comprising oxidized polyethylene wax and PVC PVC special supplements, and combined with the production process provided by the invention, to strengthen product strength and assure the quality of products.

【技术实现步骤摘要】
PVC专用强化剂
本专利技术涉及PVC生产领域，具体涉及PVC专用强化剂。
技术介绍
聚氯乙烯简称PVC，在PVC生产工艺中，经塑化的同时会有部分分子被分解，导致制品强度不理想，影响了产品质量。
技术实现思路
为解决上述技术问题，本专利技术提出了PVC专用强化剂，以达到强化制品强度和保证产品质量的目的。为达到上述目的，本专利技术的技术方案如下：一种PVC专用强化剂，包含有棉花纤维、氧化聚乙烯蜡和聚氯乙烯，其质量份数配比如下：棉花纤维10％-22％；氧化聚乙烯蜡4&-8％；聚氯乙烯70％-86％；该强化剂的制作工艺步骤如下：(1).利用氧化聚乙烯蜡对棉花纤维进行包膜；(2).将包膜后的棉花纤维与PVC进行物理链接。本专利技术通过提供一种包含有棉花纤维、氧化聚乙烯蜡和聚氯乙烯PVC专用强化剂，并结合本专利技术提供的制作工艺，达到强化制品强度和保证产品质量的目的。作为优选的，包含有棉花纤维、氧化聚乙烯蜡和聚氯乙烯，其质量份数配比如下：棉花纤维10％；氧化聚乙烯蜡4&；聚氯乙烯86％。作为优选的，包含有棉花纤维、氧化聚乙烯蜡和聚氯乙烯，其质量份数配比如下：棉花纤维16％；氧化聚乙本文档来自技高网...

【技术保护点】
一种PVC专用强化剂，其特征在于，包含有棉花纤维、氧化聚乙烯蜡和聚氯乙烯，其质量份数配比如下：棉花纤维      10％‑22％；氧化聚乙烯蜡  4&‑8％；聚氯乙烯      70％‑86％；该强化剂的制作工艺步骤如下：(1).利用氧化聚乙烯蜡对棉花纤维进行包膜；(2).将包膜后的棉花纤维与PVC进行物理链接。

【技术特征摘要】
1.一种PVC专用强化剂，其特征在于，包含有棉花纤维、氧化聚乙烯蜡和聚氯乙烯，其质量份数配比如下：棉花纤维10％-22％；氧化聚乙烯蜡4&-8％；聚氯乙烯70％-86％；该强化剂的制作工艺步骤如下：(1).利用氧化聚乙烯蜡对棉花纤维进行包膜；(2).将包膜后的棉花纤维与PVC进行物理链接。2.根据权利要求1所述的PVC专用强化剂，其特征在于，包含有棉花纤维、氧化聚乙烯蜡和聚氯乙烯，其质量份数配比...

【专利技术属性】
技术研发人员：胡伯平，
申请(专利权)人：胡伯平，
类型：发明
国别省市：浙江,33