一种利用赤泥制备金属化球团的方法及系统技术方案
Method and system for preparing metallized pellets by using red mud
The invention discloses a method and a system for preparing a metallized pellet by using red mud. The method comprises the following steps: red mud, calcium oxide, 80 to 100 DEG C hot water mixing, washing of red mud; the red mud washing after the sedimentation and filtration of red mud and water, to obtain filtrate; water will dry red mud, dry red mud; dry red mud and reducing coal mixing, molding. Get the pellet pellet; drying after direct reduction, obtaining metallized pellet. By adding calcium oxide in the process of red mud washing, the invention not only can promote the settlement of red mud, but also is beneficial to the direct reduction process of the red mud.
【技术实现步骤摘要】
一种利用赤泥制备金属化球团的方法及系统
本专利技术属于直接还原技术综合利用方向，具体地，涉及一种利用赤泥制备金属化球团的方法及系统。
技术介绍
拜耳法氧化铝生产中，需要将铝酸钠溶液与赤泥分开，赤泥再经过洗涤后进入沉降槽进行沉淀，得到赤泥进行堆存和后续的利用。由于赤泥颗粒粒度细小不匀，具有较高的比表面积，有很强的富水性能，含水率一般在60％左右，这些特殊性能，使其分离极其困难，分离需要时间超长，固液分离不清，现有技术中系长期堆放，自然晾晒，才能设法综合利用。目前为了提高国内氧化铝生产过程中赤泥沉降分离的效率，必须添加高效絮凝剂，此类絮凝剂主要依靠进口，价格昂贵，且不利于后续对赤泥的利用。
技术实现思路
针对现有技术的不足，本专利技术提供了一种利用赤泥制备金属化球团的方法，包括如下步骤：将赤泥、氧化钙、80℃～100℃的热水混合均匀，对所述赤泥进行洗涤；将洗涤后的赤泥进行沉降、过滤，获得含水赤泥和滤液；将所述含水赤泥进行干燥，获得干燥赤泥；将所述干燥赤泥与还原煤混合、成型，获得球团；将所述球团干燥后进行直接还原，获得金属化球团。在本专利技术的一些实施例中，所述氧化钙的加入...
【技术保护点】
一种利用赤泥制备金属化球团的方法，其特征在于，包括如下步骤：将赤泥、氧化钙、80℃～100℃的热水混合均匀，对所述赤泥进行洗涤；将洗涤后的赤泥进行沉降、过滤，获得含水赤泥和滤液；将所述含水赤泥进行干燥，获得干燥赤泥；将所述干燥赤泥与还原煤混合、成型，获得球团；将所述球团干燥后进行直接还原，获得金属化球团。
【技术特征摘要】
1.一种利用赤泥制备金属化球团的方法，其特征在于，包括如下步骤：将赤泥、氧化钙、80℃～100℃的热水混合均匀，对所述赤泥进行洗涤；将洗涤后的赤泥进行沉降、过滤，获得含水赤泥和滤液；将所述含水赤泥进行干燥，获得干燥赤泥；将所述干燥赤泥与还原煤混合、成型，获得球团；将所述球团干燥后进行直接还原，获得金属化球团。2.根据权利要求1所述的方法，其特征在于，所述氧化钙的加入量为干基赤泥质量的3％～20％。3.根据权利要求2所述的方法，其特征在于，所述氧化钙的加入量为干基赤泥质量的5％～15％。4.根据权利要求1所述的方法，其特征在于，所述还原煤的加入量为干基赤泥质量的10％～30％。5.一种采用权利要求1-4中任一所述方法制备金属化球团的系统，其特征在于，包括：搅拌洗涤装置，设...
【专利技术属性】
技术研发人员：王敏，古明远，吴佩佩，王健月，王福佳，曹志成，吴道洪，
申请(专利权)人：江苏省冶金设计院有限公司，
类型：发明
国别省市：江苏,32