毫米级石墨烯环状气凝胶的制备方法技术
Method for preparing millimeter grade graphene ring aerogel
The invention discloses a method for preparing graphene aerogel millimeter ring, is the use of ultrasound graphite oxide prepared by Hummers dispersed in water, then the excess water evaporation concentrated solution obtained graphene oxide, then concentrated solution of graphene oxide solution is added drop by drop into distilled water reducing agent in situ formation of graphene oxide, ring, followed by in situ reduction method to obtain millimeter ring graphene hydrogels, finally drying process to get millimeter ring graphene aerogel by freezing.
【技术实现步骤摘要】
毫米级石墨烯环状气凝胶的制备方法
本专利技术涉及一种石墨烯功能材料的制备方法。
技术介绍
纺织品印染，造纸工业，皮革鞣制等领域排放的染料废水严重破坏了人类的生活环境，引起各国政府的高度重视。如何纯化染料废水成为一个重要的研究方向。目前，染料废水的纯化方法有以下几种：絮凝法，过滤法，吸附法，光催化法等。这些方法中，吸附法具有经济效益高，设计简单，操作简单等优点，成为最具有工业应用前景的方法之一。石墨烯具有比面积大和π电子离域体系大的优点，使其成为吸附有机染料的最佳材料。（OuyangA.,WangC.,WuS.,etal,ACSAppl.Mater.Interfaces,2015,7,14439-14445）为了使吸附染料后的石墨烯更容易从水中脱离出来，科学家制备了球形或圆柱形的石墨烯气凝胶。（LiaoS.,ZhaiT.,XiaH.,J.Mater.Chem.A,2016,4,1068-1077.）然而，球形或圆柱形的气凝胶的比表面积仍比较小，因此制备的气凝胶吸附性能有限。与球形或圆柱形气凝胶相比，环形气凝胶具有更大比表面积，因此更有利于提高石墨烯气凝胶的吸附性能。...
【技术保护点】
毫米级石墨烯环状气凝胶的制备方法，其特征在于，包括以下步骤：（1）利用超声配置浓度为0.1~10 mg/ml的氧化石墨烯水溶液，然后在50~100 ℃（优选为95℃）的温度下挥发多余的水，获得浓度为1~5 wt%氧化石墨烯的浓溶液；（2）将上述氧化石墨烯的浓溶液逐滴滴加在溶有还原剂的蒸馏水中，形成氧化石墨烯环；（3）将上述含有氧化石墨烯的还原剂溶液于温度0~100℃（优选为90℃），原位还原0.1~10小时（优选为5小时）后获得石墨烯环状水凝胶；（4）将上述获得的石墨烯环状水凝胶洗涤后，利用冷冻干燥工艺获得直径为1‑10 mm的石墨烯环状气凝胶。
【技术特征摘要】
1.毫米级石墨烯环状气凝胶的制备方法，其特征在于，包括以下步骤：（1）利用超声配置浓度为0.1~10mg/ml的氧化石墨烯水溶液，然后在50~100℃（优选为95℃）的温度下挥发多余的水，获得浓度为1~5wt%氧化石墨烯的浓溶液；（2）将上述氧化石墨烯的浓溶液逐滴滴加在溶有还原剂的蒸馏水中，形成氧化石墨烯环；（3）将上述含有氧化石墨烯的还原剂溶液于温度0~100℃（优选为90℃），原位还原0.1~10小时（优选为5小时）后获得石墨烯环状水凝胶...