A polyetherimide carbon nitride floating photocatalytic material and its preparation method
The invention provides a method for preparing polyether imide carbon nitride floating photocatalytic materials, materials for the preparation of carbon nitride photocatalytic material with urea as the polyetherimide dissolved in two chloride, two chloride solution for preparing polyether imide, then carbon nitride photocatalytic material two chloride the solution into ethane polyether imide, ultrasound after centrifugation, drying precipitate to obtain the polyetherimide carbon nitride floating photocatalytic materials; the material can be effective in the degradation of methyl orange 11 watt lamp irradiation.
【技术实现步骤摘要】
一种聚醚酰亚胺-氮化碳漂浮光催化材料的制备方法
本专利技术属于光催化材料领域，具体涉及一种聚醚酰亚胺-氮化碳漂浮光催化材料的制备方法。
技术介绍
氮化碳是一类只含C、N和H等的环境友好光催化材料[张金水,王博,王心晨.氮化碳聚合物半导体光催化.化学进展,2014,26,19-29]，以尿素等为原料通过高温脱氨缩聚方法合成,耐酸耐碱，600度以上分解，没有氮流失的风险，在可见光照射下可以分解水出氢[Juan.Liu,Yang.Liu,Naiyun.Liu,Yuzhi.Han,Xing.Zhang,Hui.Huang,Yeshayahu.Lifshitz,Shuit-Tong.Lee,Jun.Zhong,Zhenhui.Kang.Metal-freeefficientphot℃atalystforstablevisiblewatersplittingviaatwo-electronpathway.Science.2015,347,970-974]、灭活水中的细菌[Wanjun.Wang,Jimmy.C.Yu,Dehua.Xia,Po.Keung.Wong;Yechen...
【技术保护点】
一种聚醚酰亚胺‑氮化碳漂浮光催化材料的制备方法，其特征在于，包括如下步骤：第一步：将尿素研磨后放入马弗炉中煅烧制得氮化碳光催化材料；第二步：将聚醚酰亚胺放入二氯乙烷中，超声后制得聚醚酰亚胺的二氯乙烷溶液；第三步：将第一步制得的氮化碳光催化材料放入第二步制得的聚醚酰亚胺的二氯乙烷溶液中，再放入超声仪器中超声处理；第四步：超声处理后将悬浊液倒入离心管中离心，干燥沉淀物即得聚醚酰亚胺‑氮化碳漂浮光催化材料。
【技术特征摘要】
1.一种聚醚酰亚胺-氮化碳漂浮光催化材料的制备方法，其特征在于，包括如下步骤：第一步：将尿素研磨后放入马弗炉中煅烧制得氮化碳光催化材料；第二步：将聚醚酰亚胺放入二氯乙烷中，超声后制得聚醚酰亚胺的二氯乙烷溶液；第三步：将第一步制得的氮化碳光催化材料放入第二步制得的聚醚酰亚胺的二氯乙烷溶液中，再放入超声仪器中超声处理；第四步：超声处理后将悬浊液倒入离心管中离心，干燥沉淀物即得聚醚酰亚胺-氮化碳漂浮光催化材料。2.根据权利要求1所述的聚醚酰亚胺-氮化碳漂浮光催化材料的制备方法，其特征在于：所述第一步氮化碳光催化材料具体制备步骤为：称量30-50g尿素，在研钵中研磨20-30min后，将其放入坩埚中，盖上坩埚盖，然后放入马弗炉中，以10℃/min的升温速度升至520-580℃，恒温40-80min后自然降温至室温，即制得淡黄色氮化碳光催化材料。3.根据权利要求1...
【专利技术属性】
技术研发人员：郭勇，王汝霞，饶磊，王沛芳，王超，
申请(专利权)人：河海大学，
类型：发明
国别省市：江苏,32