The invention discloses a preparation method and application of a SiO2@ZnO core shell multiped ball nano composite material, the method is through the growth of ZnO crystal in situ SiO2 ball surface, after growth in solution by sonication, and static separation, washing and drying to obtain SiO2@ZnO core-shell structure nano composite multiped ball material. The method of ultrasonic wave grinding is applied to prepare in situ growth method with mild condition and simple process, which is suitable for large area production. SiO2@ZnO core-shell structure composite multiped ball size prepared by the invention is uniform, good dispersion, controllable components, is expected to be applied to the photoelectric material or photocatalytic materials etc..
【技术实现步骤摘要】
一种SiO2@ZnO核壳结构多足小球纳米复合材料的制备方法及其应用
本专利技术属于纳米复合新材料
，具体涉及一种SiO2@ZnO核壳结构多足小球纳米复合材料的制备方法及其应用。
技术介绍
ZnO是一种典型的宽禁带直接带隙半导体材料，具有良好的生物相容性和环境安全性，近年来作为一种很有前景的光催化材料而受到广大科研工作者的广泛关注。众所周知，光催化剂的结构、形貌、表面状态等因素直接影响其性能和应用。通过对制备工艺和条件的控制，获得了多种尺寸和形貌的ZnO纳米材料，大大提高了其光催化活性。ZnO纳米材料在实际应用中存在纳米尺寸材料易团聚、对有机物吸附性能较差、量子产率偏低等缺陷，这些大大限制了ZnO光催活性的提高及其应用。基于此，出现了一些ZnO/半导体异质结复合材料，其制备方法多为水热/溶剂热。如SiO2与ZnO复合，其结构多为简单纳米粒子或者以ZnO为核，SiO2胶体为壳形成的球形纳米颗粒。SiO2与ZnO复合后，一些性能如光致发光性能得到了提高。水热/溶剂热法需要密闭的高温高压环境，不适宜大面积生产。超声粉碎制备材料简便、快速、适合大面积制备等优点。目前采...
【技术保护点】
一种SiO2@ZnO核壳结构多足小球纳米复合材料的制备方法，其特征在于，所述方法是通过在SiO2小球表面原位生长ZnO晶种，之后在生长溶液中超声粉碎，然后经静置分离、洗涤和干燥后得到SiO2@ZnO核壳结构多足小球纳米复合材料。
【技术特征摘要】
1.一种SiO2@ZnO核壳结构多足小球纳米复合材料的制备方法，其特征在于，所述方法是通过在SiO2小球表面原位生长ZnO晶种，之后在生长溶液中超声粉碎，然后经静置分离、洗涤和干燥后得到SiO2@ZnO核壳结构多足小球纳米复合材料。2.根据权利要求1所述SiO2@ZnO核壳结构多足小球纳米复合材料的制备方法，其特征在于，所述SiO2小球表面原位生长ZnO晶种是将带负电的SiO2小球加入到带正电的ZnO晶种溶液中，经振荡过滤后得到带有ZnO晶种的SiO2小球。3.根据权利要求2所述SiO2@ZnO核壳结构多足小球纳米复合材料的制备方法，其特征在于，所述SiO2小球与ZnO晶种溶液的质量浓度比为0.01g:0.2-1.0g/L。4.根据权利要求1所述Si...
【专利技术属性】
技术研发人员：冒国兵，刘琪，周贝贝，刘荣梅，
申请(专利权)人：安徽工程大学，
类型：发明
国别省市：安徽,34