The invention discloses a method for improving asphalt or modified asphalt low temperature ductility and ductility after aging additives composed of groups the following parts by weight: A group: 20 phosphate 40, group B: 60 80 aromatic oil. The invention also discloses the preparation method of the additive. The production process of the invention is simple, the cost is low, and the production is easy to be industrialized. Add to the proportion of asphalt is low, approximately between 0.5 and 1.5%, additive of the invention product itself and index of asphalt asphalt mixture can obviously improve the index no harm, asphalt or modified asphalt ductility at low temperature, and low temperature ductility after aging, and does not affect the asphalt or modified the asphalt softening point and penetration.
【技术实现步骤摘要】
改善沥青或改性沥青低温延度及老化后延度的添加剂及其制备方法
本专利技术涉及化工产品制备领域，特别涉及一种改善沥青或改性沥青低温延度及老化后延度的添加剂及其制备方法。
技术介绍
沥青或改性沥青在高温存储，运输，生产混合料过程中，由于持续高温会使得沥青老化，从而使得沥青的低温性能降低。目前见诸报道的用于改善沥青老化性能添加剂有稀土元素氧化物；改性蒙脱土、抗氧化剂、光稳定剂的混合物。其中稀土元素氧化物、抗氧化剂、光稳定剂成本过高，改性蒙脱土和沥青的相容性都限制了这些方案工业化生产和运用。
技术实现思路
本专利技术要解决的技术问题是提供一种改善沥青或改性沥青低温延度及老化后延度的添加剂。为了解决上述技术问题，本专利技术的技术方案为：一种改善沥青或改性沥青低温延度及老化后延度的添加剂，由下列重量份数的各组份组成：组份A：磷酸酯20-40份，组份B：芳烃油60-80份。作为优选，所述的磷酸酯的结构式为PO(OR)n，其中n＝1-3，R代表碳原子数1-18的烷基。作为优选，所述的组份B为渣油、重油、糠醛抽出油。本专利技术还公开了上述添加剂的制备方法和使用方法：将上述组份A和组份B混合均匀，即得。将沥青重量0.5-1.5％的添加剂加到沥青中。沥青的热老化过程是由于在加热过程中沥青中的小分子聚合成大分子，从而导致沥青中沥青质这一组分大幅度增加，芳香分这一组分减少，本专利技术中含有的磷酸酯能够阻碍或减少沥青中的小分子在加热过程中聚合成大分子，芳烃油能够调节沥青中沥青质和芳香分的比例，进一步减少持续高温对沥青造成的老化。本专利技术的生产工艺简单，成本低，易于工业化生产。添加到沥青中...
【技术保护点】
一种改善沥青或改性沥青低温延度及老化后延度的添加剂，其特征在于：由下列重量份数的各组份组成：组份A：磷酸酯20‑40份，组份B：芳烃油60‑80份。
【技术特征摘要】
1.一种改善沥青或改性沥青低温延度及老化后延度的添加剂，其特征在于：由下列重量份数的各组份组成：组份A：磷酸酯20-40份，组份B：芳烃油60-80份。2.如权利要求1所述的改善沥青或改性沥青低温延度及老化后延度的添加剂，其特征在于：所述的磷酸酯的结构式为PO(OR)n，其中n＝1-3，R代表碳原子数1-18的烷基。3.如权利要求1或2所述的改善沥青或改性沥...