The invention belongs to the field of surface treatment agent, in particular to a glass fiber surface treating agent and application thereof. The glass fiber surface treatment agent provided by the invention comprises fluoropolymer emulsion, silicone oil emulsion, cross-linking agent, surface active agent, water treatment agent and related media; in the content of fluoropolymer emulsion is 25 ~ 45wt%, the content of silicone oil emulsion is 0.2 ~ 10wt%, the content of crosslinking agent is 0.2 ~ 1wt%, the content of surface the active agent is 0.2 ~ 2wt%, the content of related media is 0.5 ~ 2wt%. The invention was optimized by the composition and content of each treatment points, obtained a suitable for the treatment of glass fiber surface treatment agent, folding and excellent wear resistance provided by the invention of the surface treatment agent treated glass fiber fabric.
【技术实现步骤摘要】
一种玻纤表面处理剂及其应用
本专利技术属于表面处理剂领域，尤其涉及一种玻纤表面处理剂及其应用。
技术介绍
近年来，随着全球对环保的日益重视，环保产业呈现出高速发展的态势。钢铁、冶金、化工、电力等烟气的粉尘治理大量采用袋式除尘法。而工业生产中产生的高温含尘烟气一般来说具有自身的特点：烟气浓度较高，波动较大；烟气温度高；含有酸性气体和湿气，具有一定的腐蚀性。鉴于燃煤烟气其苛刻的工况条件，许多厂家使用PPS纤维、P84纤维和PTFE纤维制作过滤材料。而这几种纤维的价格都比较高，且不同程度的存在耐腐蚀性差、耐水解性差、耐高温性差等缺点。玻璃纤维具有优异的耐高温性能，对多数酸的耐蚀性也较好，且价格低廉，理论上应该是替代上述几种纤维作为袋式除尘器过滤材料的理想材料。但玻璃纤维的耐折和耐磨性极差，其作为过滤材料应用到袋式除尘器中时，在脉冲清灰时很容易被损坏。
技术实现思路
有鉴于此，本专利技术的目的在于提供一种玻纤表面处理剂及其应用，采用本专利技术提供的表面处理剂处理得到的玻璃纤维织物耐折和耐磨性能优异。本专利技术提供了一种玻纤表面处理剂，包括氟聚物乳液、硅油乳液、交联剂、表面活性...
【技术保护点】
一种玻纤表面处理剂，包括氟聚物乳液、硅油乳液、交联剂、表面活性剂、关联介质和水；处理剂中，氟聚物乳液的含量为25～45wt％，硅油乳液的含量为0.2～10wt％，交联剂的含量为0.2～1wt％，表面活性剂的含量为0.2～2wt％，关联介质的含量为0.5～2wt％。
【技术特征摘要】
1.一种玻纤表面处理剂，包括氟聚物乳液、硅油乳液、交联剂、表面活性剂、关联介质和水；处理剂中，氟聚物乳液的含量为25～45wt％，硅油乳液的含量为0.2～10wt％，交联剂的含量为0.2～1wt％，表面活性剂的含量为0.2～2wt％，关联介质的含量为0.5～2wt％。2.根据权利要求1所述的处理剂，其特征在于，所述氟聚物乳液包括聚四氟乙烯乳液和/或聚四氟六氟共聚物乳液。3.根据权利要求2所述的处理剂，其特征在于，所述氟聚物乳液的固含量为40～70wt％；所述氟聚物乳液中氟聚物的数均分子量为1000000～2000000。4.根据权利要求1所述的处理剂，其特征在于，所述硅油乳液包括甲基硅油乳液、苯甲基硅油乳液、羟基硅油乳...