建筑密封胶配方组成比例

本发明专利技术公开了一种建筑密封胶配方，涉及建筑材料领域，该建筑密封胶配方采用聚醚多元醇、二苯基甲烷二异氰酸酯、邻苯二甲酸二丁酯、蓖麻油、钛白粉、聚醚多元醇、触变剂、防老剂、干燥剂为原料。具有优良的耐磨性，低温柔软性，性能可调节范围较广，机械强度大，粘接性好，弹性好，具有优良复原性，可适合于动态接缝，耐候性好，使用寿命可达15～20年；耐油性能优良，耐生物老化。

Building sealant formula

The invention discloses a building sealant formulation, relates to the field of building materials, the building sealant formulations with polyether polyols, two phenyl methane diisocyanate, dibutyl phthalate, castor oil, titanium dioxide, polyether polyol, thixotropic agent, anti-aging agent, drying agent as raw materials. With excellent wear resistance, low temperature flexibility, performance can be adjusted in a wide range, high mechanical strength, good adhesion, good elasticity, excellent resilience, can be suitable for the dynamic joint, good weather resistance, service life of up to 15 to 20 years; excellent oil resistance, resistance to biological aging.

【技术实现步骤摘要】
建筑密封胶配方
本专利技术涉及建筑材料领域，更具体地说，本专利技术涉及一种建筑密封胶配方。
技术介绍
建筑密封胶是用来将不同的建筑材料牢固粘贴在一起的粘结剂，建筑密封胶大多具有良好的粘性。现有的建筑密封胶用材比较传统，使用时不能长期耐热，浅色配方容易受紫外光老化，单组分胶贮存稳定性受包装及外界影响较大，通常固化较慢，高温热环境下可能产生气泡和裂纹。
技术实现思路
本专利技术所要解决的问题是提供一种建筑密封胶配方，具有优良的耐磨性，低温柔软性，性能可调节范围较广，机械强度大，粘接性好，弹性好，具有优良复原性，可适合于动态接缝。为了实现上述目的，本专利技术采取的技术方案为：一种建筑密封胶配方，其特征在于，该建筑密封胶配方包括如下重量份数的原料：25～32份聚醚多元醇、22～28份二苯基甲烷二异氰酸酯、22～28份邻苯二甲酸二丁酯、10～15份蓖麻油、10～15份钛白粉、16～22份聚醚多元醇、3～7份触变剂、0.2～0.8份防老剂、0.2～0.8份干燥剂。优选的，所述建筑密封胶配方包括如下重量份数的原料：25份聚醚多元醇、22份二苯基甲烷二异氰酸酯、28份邻苯二甲酸二丁酯、10份蓖麻油、15本文档来自技高网...

【技术保护点】
一种建筑密封胶配方，其特征在于，该建筑密封胶配方包括如下重量份数的原料：25～32份聚醚多元醇、22～28份二苯基甲烷二异氰酸酯、22～28份邻苯二甲酸二丁酯、10～15份蓖麻油、10～15份钛白粉、16～22份聚醚多元醇、3～7份触变剂、0.2～0.8份防老剂、0.2～0.8份干燥剂。

【技术特征摘要】
1.一种建筑密封胶配方，其特征在于，该建筑密封胶配方包括如下重量份数的原料：25～32份聚醚多元醇、22～28份二苯基甲烷二异氰酸酯、22～28份邻苯二甲酸二丁酯、10～15份蓖麻油、10～15份钛白粉、16～22份聚醚多元醇、3～7份触变剂、0.2～0.8份防老剂、0.2～0.8份干燥剂。2.按照权利要求1所述的一种建筑密封胶配方，其特征在于：所述建筑密封胶配方包括如下重量份数的原料：25份聚醚多元醇、22份二苯基甲烷二异氰酸酯、28份邻苯二甲酸二丁酯、10份蓖麻油、15份钛白粉、22份聚醚多元醇、3份触变剂、0.8份防老剂...

【专利技术属性】
技术研发人员：张科强，
申请(专利权)人：陕西理工大学，
类型：发明
国别省市：陕西,61