The invention discloses a high efficiency inhibitor and preparation method and application thereof, wherein the efficient compound corrosion inhibitor comprises twelve sodium dodecyl sulfate 0.1~1.0 g/L 0.05~0.5 g/L, polyvinyl alcohol, butyl ketone oxime 0.05~0.1 two g/L, protocatechuic aldehyde 0.01~0.05 g/L margin for acid pickling. The invention has the obvious inhibitory effect of hydrochloric acid and corrosion of aluminum corrosion between high efficiency and obvious synergistic effect, strong adaptability, good effect and high temperature, suitable for aluminum in hydrochloric acid cleaning, cleaning can be used in petrochemical equipment, boilers, aluminum, pipelines and other equipment of the invention. The inhibitor is safe and easy to use, simple operation, quick.
【技术实现步骤摘要】
一种高效复配缓蚀剂及其制备方法与应用
本专利技术属于金属缓蚀剂
，具体涉及一种高效复配缓蚀剂及其制备方法与应用。
技术介绍
金属材料在现代工农业、机械、交通、运输、国防和科学技术等部门占有非常重要的地位。金属铝具有外观美、质量轻、导热、导电性能好等优点，在国民经济各部门得到极其广泛的应用。铝在使用过程中会形成一层氧化膜，这层氧化膜较为脆弱和疏松，会使铝失去光泽，且直接在铝材料上涂装，会使涂膜的附着力不强，为此需对铝进行表面预处理，以除去氧化膜，其中对铝进行酸洗是较为常用的方法。此外，铝材料设备在使用过程中会留有大量赃物或垢层，为了清除赃物和垢层，采用酸洗是一种较为方便的方法。铝为活泼金属，在酸溶液中会发生剧烈析氢腐蚀，故在化学工业中为了保护铝基体免受酸的进一步腐蚀，需在酸洗液中需添加酸洗缓蚀剂。盐酸价格便宜，清洗速度快。铬酸盐是铝的传统优良的缓蚀剂，但由于这些铬酸盐会致癌和污染环境，故近年来已被禁止或限制应用。目前工业使用的缓蚀剂大多为两种或两种以上的复配有机缓蚀剂，主要利用它们之间的协同效应来提高缓蚀效果。与单一缓蚀剂相比，复配缓蚀剂具有缓蚀效果好、性能稳...
【技术保护点】
一种高效复配缓蚀剂，其特征在于所述的高效复配缓蚀剂包括阴离子表面活性剂0.1~1.0 g/L，高分子化合物0.05~0.5 g/L，肟类化合物0.05~0.1 g/L，芳香醛类化合物0.01~0.05 g/L，余量为酸洗液。
【技术特征摘要】
1.一种高效复配缓蚀剂，其特征在于所述的高效复配缓蚀剂包括阴离子表面活性剂0.1~1.0g/L，高分子化合物0.05~0.5g/L，肟类化合物0.05~0.1g/L，芳香醛类化合物0.01~0.05g/L，余量为酸洗液。2.根据权利要求1所述的高效复配缓蚀剂，其特征在于所述的阴离子表面活性剂为十二烷基硫酸钠。3.根据权利要求1所述的高效复配缓蚀剂，其特征在于所述的高分子化合物为聚乙烯醇。4.根据权利要求1所述的高效复配缓蚀剂，其特征在于所述的肟类化合物为丁二酮肟。5.根据权利要求1所述的高效复配缓蚀剂，其特征在于所述的芳香醛类化合物为原儿茶醛。6.根据权利要求1所述的高效复配缓蚀剂，其特征在于所述的酸洗液为盐酸。7.根据权利...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。