The present invention discloses a filling method for expanded perlite. Method for filling the expanded perlite, the specific steps are as follows: (1), will be ready to 160 degrees above the expanded perlite filling heating; (2), the heating of the expanded perlite into the charging valve and the tank needs to fill the vacuum processing; (3), the first vibrator is opened, and then open the feeding when the valve plug tank gas by compaction of expanded perlite filling port; (4), close the charging valve, then close the vibrator; (5) and vacuum treatment on storage tank; (6), repeat steps (3) ~ (5) until the storage tank of the expanded perlite density reached 90 ~ 110 kg per cubic meter. The filling method of the expanded perlite greatly shortens the time required for filling and improves the filling efficiency.
【技术实现步骤摘要】
膨胀珍珠岩的填充方法
本申请涉及膨胀珍珠岩应用领域，特别涉及一种膨胀珍珠岩的填充方法。
技术介绍
膨胀珍珠岩是珍珠岩矿砂经预热，瞬时高温焙烧膨胀后制成的一种内部为蜂窝状结构的白色颗粒状的材料。其原理为:珍珠岩矿石经破碎形成一定粒度的矿砂，经预热焙烧，急速加热，矿砂中水分汽化，在软化的含有玻璃质的矿砂内部膨胀，形成多孔结构，具有良好的保温性能，而储罐的外壳和内胆之间真空并填充有膨胀珍珠岩来进行保温，现有填充方法耗时巨大，容易造成无法及时填充及填充空间无法周转，生产效率低下。故此需要提出改进。
技术实现思路
本专利技术的目的在于提供一种制造膨胀珍珠岩的膨胀珍珠岩的填充方法，以克服现有技术中的不足。为实现上述目的，本专利技术提供如下技术方案：本申请实施例公开了一种膨胀珍珠岩的填充方法，其具体步骤如下：(1)、将准备填充的膨胀珍珠岩加热到160℃以上；(2)、将加热后的膨胀珍珠岩送入加料阀，同时对需要填充的储罐夹层空间进行抽真空处理；(3)、首先开启振动器，然后开启加料阀，当发生膨胀珍珠岩堵塞储罐填充口时利用气体压实；(4)、关闭加料阀，然后关闭振动器；(5)、对储罐夹层进行...
【技术保护点】
一种膨胀珍珠岩的填充方法，用以将膨胀珍珠岩填充至储罐的侧壁夹层中，其特征在于具体步骤如下：(1)、将准备填充的膨胀珍珠岩加热到160℃以上；(2)、将加热后的膨胀珍珠岩送入加料阀，同时对需要填充的储罐夹层空间进行抽真空处理；(3)、首先开启振动器，然后开启加料阀，当发生膨胀珍珠岩堵塞储罐填充口时利用气体压实；(4)、关闭加料阀，然后关闭振动器；(5)、对储罐夹层进行抽真空处理；(6)、重复步骤(3)～(5)直至储罐内的膨胀珍珠岩密度达到90～110千克每立方米和储罐夹层完全真空。
【技术特征摘要】
1.一种膨胀珍珠岩的填充方法，用以将膨胀珍珠岩填充至储罐的侧壁夹层中，其特征在于具体步骤如下：(1)、将准备填充的膨胀珍珠岩加热到160℃以上；(2)、将加热后的膨胀珍珠岩送入加料阀，同时对需要填充的储罐夹层空间进行抽真空处理；(3)、首先开启振动器，然后开启加料阀，当发生膨胀珍珠岩堵塞储罐填充口时利用气体压实；(4)、关闭加料阀，然后关闭振动器；(5)、对储罐夹层进行抽真空处理；(6)、重复步骤(3)～(5)直至储罐内的膨胀珍珠岩密度达到90～110千克每立方米和储罐夹层完全真空。2.根...