The invention relates to a three yuan of benzoxazine phthalate two cyano intermediates, preparation method and polymer preparation method comprises the following steps: 1) added to the reactor type II 4 compounds, amino phenoxy phthalate two cyano, paraformaldehyde and mixed solvent, heating up to 80 to 130 DEG C; the mixed solvent of two oxygen ring and six toluene; 2) removal of mixed solvent, the residue is dissolved in a solvent, and pouring into the alkali liquid, solid precipitation, filtration, washing, drying to obtain three yuan of benzoxazine phthalate two cyano intermediates. The three yuan of benzoxazine phthalate two cyano intermediate good processability, curing the polymer with excellent comprehensive properties.
【技术实现步骤摘要】
一种三元苯并噁嗪-邻苯二甲腈中间体、制备方法及其聚合物
本专利技术涉及高性能热固性树脂制备
，具体涉及一种三元苯并噁嗪-邻苯二甲腈中间体、制备方法及其聚合物。
技术介绍
双邻苯二甲腈树脂是一类高性能热固性树脂，由双邻苯二甲腈单体在高温条件下通过氰基的加聚反应固化而成，固化物以三嗪环结构为主。该树脂及其复合材料具有高强度、高模量、耐高温、抗腐蚀、自阻燃，固化过程无小分子释放，制品孔隙率低，接近零收缩，热膨胀系数低、尺寸稳定、低吸水率等特点。完全固化后Tg可达到450℃以上。虽然双邻苯二甲腈树脂具有诸多优异的应用性能，但存在固化温度高(起始固化温度为240℃左右)，加工窗口窄的缺点。苯并噁嗪是一类由酚类化合物、胺类化合物和醛类化合物经缩合反应合成的六元杂环化合物，在加热或催化剂作用下开环聚合，生成含氮且类似酚醛树脂的网状结构。苯并噁嗪树脂作为一种新型的酚醛树脂，其不仅具有传统酚醛树脂的热性能、力学性能、电性能、阻燃性及耐腐蚀性，且固化成型时收缩率小，无小分子释放，吸水率低。与双邻苯二甲腈树脂相比，苯并噁嗪树脂固化温度低，起始固化温度为150℃左右，但起始分解温度...
【技术保护点】
一种三元苯并噁嗪‑邻苯二甲腈中间体，其特征在于，结构式如下：
【技术特征摘要】
1.一种三元苯并噁嗪-邻苯二甲腈中间体，其特征在于，结构式如下：其中，R1～R6各自独立地选自氢或C1～C4烷基。2.一种三元苯并噁嗪-邻苯二甲腈中间体的制备方法，其特征在于，包括如下步骤：1)向反应器中加入式Ⅱ化合物、4-氨基苯氧基邻苯二甲腈、多聚甲醛和混合溶剂，升温至80～130℃反应；所述混合溶剂为二氧六环和甲苯；其中，R1～R6各自独立地选自氢或C1～C4烷基，且酚羟基邻位不能同时为烷基；2)除去混合溶剂，将剩余物溶解在溶剂中，并倾倒至碱液中，析出固体，过滤，洗涤，干燥后得到三元苯并噁嗪-邻苯二甲腈中间体。3.根据权利要求2所述的三元苯并噁嗪-邻苯二甲腈中间体的制备方法，其特征在于，所述步骤1)中反应为避光反应。4.根据权利要求2所述的三元苯并噁嗪-邻苯二甲腈中间体的制备方法，其特征在于，所述步骤1)中4-氨基苯氧基邻苯二甲腈与多聚甲醛按氨基和醛基的摩尔配比为1:1.7～2.5投料。5.根据权利要求2所述的三元...
【专利技术属性】
技术研发人员：方仕江，彭学刚，
申请(专利权)人：常州焱晶科技有限公司，
类型：发明
国别省市：江苏,32