一种CdS/ZnFe2O4复合光催化剂及其制备方法技术

本发明专利技术公开了一种CdS/ZnFe2O4复合光催化剂及其制备方法，通过水热法制备CdS纳米颗粒，然后通过水热法在CdS表面沉积ZnFe2O4纳米颗粒。按照本发明专利技术制备出立方相CdS，并以此为载体，负载ZnFe2O4纳米颗粒，增加了光催化剂的比表面积，降低了电子空穴复合率，提高了CdS的光催化活性，能够有效降解污水中的有机染料。

CdS/ZnFe2O4 composite photocatalyst and preparation method thereof

The invention discloses a CdS/ZnFe2O4 composite photocatalyst and a preparation method thereof, wherein CdS nanoparticles are prepared by hydrothermal process, and then ZnFe2O4 nanoparticles are deposited on the surface of CdS by hydrothermal method. According to the invention prepared cubic phase CdS, and as the carrier, loaded ZnFe2O4 nanoparticles, increase the specific surface area of the photocatalyst, reduce the electron hole recombination rate, increase the photocatalytic activity of CdS, can effectively degrade organic dyes in wastewater.

【技术实现步骤摘要】
一种CdS/ZnFe2O4复合光催化剂及其制备方法
本专利技术属于无机功能材料
，涉及一种光催化剂及制备方法，具体涉及一种CdS/ZnFe2O4复合光催化剂及其制备方法。
技术介绍
目前人们开发的许许多多半导体光催化剂如TiO2、钽酸盐、铌酸盐等带隙较宽，使得光催化剂只有在紫外光范围才能发生响应，而太阳光总能量中仅有5％波长位于400nm以下的紫外光部分，显然不足以实现有效利用，同时我们知道太阳光能量主要集中可见光范围，一般波长为400-700nm，这部分能量占到总能量的43％左右。因此为提高太阳能利用率，最终实现光催化技术产业化应用，研制具有可见光响应的且转换效率较高的光催化剂势在必行。CdS是一种典型的Ⅱ-Ⅵ族半导体材料，属于直接带隙半导体化合物，CdS的禁带宽度为2.4eV，具有良好的发光性能和光电转换特性，在发光二级管、光电器件、太阳能电池、光催化、非线性光学等领域有着广泛的应用。在使用CdS单独作为光催化剂时，存在光腐蚀现象，降低了光生空穴的利用率。JialiZhai,etal.,(ACSAppl.Mater.,Interfaces,2011,3,2253-2258)本文档来自技高网...

【技术保护点】
一种CdS/ZnFe2O4复合光催化剂，其特征在于，其中，CdS/ZnFe2O4中CdS与ZnFe2O4的摩尔比为1:1‑3:1。

【技术特征摘要】
1.一种CdS/ZnFe2O4复合光催化剂，其特征在于，其中，CdS/ZnFe2O4中CdS与ZnFe2O4的摩尔比为1:1-3:1。2.如权利要求1所述的光催化剂，其特征在于，由如下步骤制备：将一定量的CdS超声分散到Zn(NO3)2和Fe(NO3)3的混合水溶液中，调节pH值后进行水热反应，将得到的沉淀洗涤离心烘干，得到CdS/ZnFe2O4粉末。3.如权利要求2所述的光催化剂，其特征在于，CdS与Z...