The invention discloses a liquid metal thermal interface material gain performance, is divided into three layers, the middle layer is composed of the following components in weight percentage: Zn:1.0 4%, Bi:2.0 6%, Sn:10.0 40%, Au:0.3 0.8%, V:0.1 0.2%, allowance for In; on the two floor above have in addition to the alloy composition also, including the second phase particles, the second phase particles of Cu, Ti, Mo, W and O, N, S, compound P formation. The product in the maintenance of the liquid metal thermal interface materials with high thermal conductivity (20 85W / m.K) at the same time, the thermal interface materials in normal working condition to maintain solid state, thus effectively filling the heating body and the heating body micron pore surface. In the case of liquid metal working in solid state, the occurrence of side leakage has been fundamentally avoided.
【技术实现步骤摘要】
具有自增益性能的液态金属热界面材料
本专利技术涉及液态金属材料，具体地说，涉及具有自增益性能的液态金属热界面材料。
技术介绍
众所周知，IGBT器件以其输入阻值高、开关速度快、通态电压低、阻断电压高、承受电流大等特点，已成为当今功率半导体器件发展的主流器件，广泛应用到各种交流电机、变频器、开关电源、照明电路、牵引传动等领域功率电子电路中。当IGBT器件工作时，产生的热量会使芯片温度迅速上升超过最大允许IGBT结温。因此，IGBT的性能将大大降低，而不能稳定工作，导致性能下降或失效。近年来由于IGBT技术的进一步发展，相关的极端环境下的高效散热技术已经成为热管理工程师和科学家都渴望解决的关键技术问题。完整的IGBT模块包括IGBT器件、散热器、热风扇以及导热介质四部分组成，其中IGBT器件本身和导热介质对散热性能起决定性作用。发热体和散热体之间的接触面有微观上的孔洞，中间充满了空气。因为空气是不良热导体，发热体和散热器之间的热界面电阻非常大，严重阻碍了热传导，最终导致低散热效率。具有高导热系数的热界面材料可以填充这些微观上的空隙，有助于建立有效的热传导通道，从而大大...
【技术保护点】
一种具有自增益性能的液态金属热界面材料，其特征在于为三层结构，中间层由如下重量百分数的组分组成：Zn：1.0‑4.0%, Bi: 2.0‑6.0%, Sn: 10.0‑40.0%, Au: 0.3‑0.8%, V: 0.1‑0.2%,余量为In；上下两层除了具备如上的合金成分，还包括第二相颗粒，所述第二相颗粒为Cu, Ti,Mo,W和O¸N, S, P形成的化合物。
【技术特征摘要】
1.一种具有自增益性能的液态金属热界面材料，其特征在于为三层结构，中间层由如下重量百分数的组分组成：Zn：1.0-4.0%,Bi:2.0-6.0%,Sn:10.0-40.0%,Au:0.3-0.8%,V:0.1-0.2%,余量为In；上下两层除了具备如上的合金成分，还包括第二相颗粒，所述第二相颗粒为Cu,Ti,Mo,W和O¸N,S,P形成的化合物。2.如权利要求1所述的具有自增益性能的液态金属热界面材料，其特征在于所述上下两层具备第二相颗粒的厚度均占总厚度的5%，第二相颗粒在所在层的体积分数为5-1...
【专利技术属性】
技术研发人员：刘亚军，曹贺全，曹帅，郭强，吴智鑫，
申请(专利权)人：宁波新瑞清科金属材料有限公司，
类型：发明
国别省市：浙江,33