一种激光微熔凝弥合金属表面微裂纹的方法技术

本发明专利技术提供了一种基于激光微熔凝修复金属表面微裂纹的方法，属于激光加工领域。使用长脉冲激光或者连续激光束扫描金属工件表面，利用激光的热效应使微裂纹区域微熔化，微熔化的金属液体发生流动，流向微裂纹区域后再凝固，从而达到弥合金属表面微细裂纹的效果。本发明专利技术所述的基于激光微熔凝弥合金属表面微裂纹的方法，不需要外加材料，工艺简单，方便操作，生产效率高，无环境污染，易于实现自动化生产，有利于工业上大规模推广。

Laser micro fusion method for bridging micro cracks on metal surface

The invention provides a method for repairing metal surface micro cracks based on laser micro melting, belonging to the field of laser processing. The use of long pulse laser and continuous laser beam scanning surface of metal workpiece, the micro crack area of micro melting with heat effect of laser melting metal, liquid micro flow, the flow of the micro crack area after solidification, so as to bridge the metal surface micro crack effect. The invention of laser micro cladding metal bridge surface micro crack based method, and does not need additional material, simple process, convenient operation, high production efficiency, no pollution, easy to realize automation of production, is conducive to large-scale promotion of industry.

【技术实现步骤摘要】
一种激光微熔凝弥合金属表面微裂纹的方法
本专利技术涉及激光微加工领域，尤其涉及一种激光微熔凝弥合金属表面微裂纹的方法。
技术介绍
金属零部件在加工或使用过程中，由于材料自身特性、加工过程或者使用过程中产生应力、腐蚀、磨损等，使工件表面产生尺寸为纳米量级或者微米量级的微裂纹。例如：硬质合金呈脆性，且自身硬度较高，在加工成刀具的过程中表面容易产生微裂纹，从而影响刀具使用寿命；汽轮机或水轮机的叶片的在工作过程中受到流体的冲击，长期运行后，叶片表面会产生疲劳裂纹。以往，这些带有微裂纹的零部件，或者被报废抛弃，或者“带伤”继续使用直至彻底无法使用后被报废抛弃，造成能源和材料的浪费。因此，对带微裂纹零部件进行裂纹修复，对节约成本、提高工件的利用率，以及节能环保都非常必要。目前，金属表面裂纹修复的方法众多，针对不同尺度的裂纹，选择修复的方法也不同。如机械类重锤敲击技术，通过对金属表面施加高应力载荷，改变金属表面应力状态，减缓甚至消除金属表面的裂纹扩张，在一定程度上可延长工件使用寿命。电化学类的方法主要有：离子注入，电镀等。离子注入法是指在真空系统中，将经过加速的要掺杂的原子，通过离子注入法注入微裂本文档来自技高网...

【技术保护点】
一种激光微熔凝弥合金属表面微裂纹的方法，其特征在于，使用激光束扫描金属工件表面微裂纹区域，利用激光的热效应使金属工件表面微裂纹区域微熔化形成金属液体，所述金属液体发生流动，流入微裂纹区域后再凝固，从而达到弥合金属表面裂纹的效果。

【技术特征摘要】
1.一种激光微熔凝弥合金属表面微裂纹的方法，其特征在于，使用激光束扫描金属工件表面微裂纹区域，利用激光的热效应使金属工件表面微裂纹区域微熔化形成金属液体，所述金属液体发生流动，流入微裂纹区域后再凝固，从而达到弥合金属表面裂纹的效果。2.根据权利要求1所述的激光微熔凝弥合金属表面微裂纹的方法，其特征在于，所述激光束为长脉冲激光束或者连续激光束，以实现金属工件表面微裂纹区域微熔。3.根据权利要求2所述的激光微熔凝弥...

【专利技术属性】
技术研发人员：叶云霞，陈美，左慧，康正阳，任旭东，
申请(专利权)人：江苏大学，
类型：发明
国别省市：江苏,32