一种钢板用水性无铬快速成膜处理液及其制备方法技术

本发明专利技术公开一种钢板用水性无铬快速成膜处理液，其成分包括：硫脲6～10g/L，丁二酸15～17g/L，硼酸0.9～1.1g/L，对氨基苯磺酸盐4～6g/L，磷酸二氢锌2～4g/L。本发明专利技术中处理液成分简单，易于控制，不含有机易挥发物质，工艺稳定。本发明专利技术处理时间短，固化温度低，适于工业化生产。本发明专利技术制得的转化膜膜层均匀，耐蚀性好。本发明专利技术处理液不含任何形式的铬元素，所以环境负担小，满足绿色化学发展趋势。

Water chromium free fast film forming treatment liquid for steel plate and preparation method thereof

The invention discloses a plate of water film processing liquid chromium rapidly, its components include: thiourea 6 ~ 10g/L, 15 ~ 17g/L succinic acid, boric acid is 0.9 ~ 1.1g/L, sulfanilate 4 ~ 6g/L, two ~ 2 4g/L zinc phosphate. The method has the advantages of simple liquid composition, easy control, no volatile matter and stable process. The invention has short processing time and low curing temperature and is suitable for industrial production. The conversion film prepared by the invention has uniform film and good corrosion resistance. The treatment liquid of the invention does not contain chromium in any form, so the environmental burden is small, and the development trend of green chemistry is satisfied.

【技术实现步骤摘要】
一种钢板用水性无铬快速成膜处理液及其制备方法
本专利技术涉及钢板表面处理技术，特别涉及一种钢板用水性无铬快速成膜处理液及其制备方法。
技术介绍
目前为了防止钢板在长期储存和运输过程中发生锈蚀问题，钢板表面均涂布一定量的防锈油，但涂布防锈油经常导致下卷过程中抽芯打滑现象。且随着环境保护意识的提高和绿色化学技术的不断发展，在钢板使用加工过程中清洗防锈油产生的含油废水引起的环境问题被日益关注。采用环境友好的水性无铬化学转化膜替代涂油防腐蚀的工艺是一种具有发展前景的解决方案。专利CN1875123B公布了化学转化成膜性能优良的热轧钢板及其制造方法，其采用浸渍处理液的方法制备钢板表面钝化膜，但需要一定的浸渍时间以保证成膜的连续性。
技术实现思路
本专利技术提供一种钢板用无铬快速成膜处理液及其制备方法，提供反应速度快、常温即成膜的具有优良耐蚀性的、对环境影响小的无铬处理液。为解决上述技术问题，本专利技术专利技术采用如下技术方案：一种钢板用水性无铬快速成膜处理液的成分包括：硫脲6～10g/L；丁二酸15～17g/L；硼酸0.9～1.1g/L；对氨基苯磺酸盐4～6g/L；磷酸二氢锌2～4g/L。以下对本本文档来自技高网...

【技术保护点】
一种钢板用水性无铬快速成膜处理液，其特征在于，处理液的成分包括：硫脲6～10g/L；丁二酸15～17g/L；硼酸0.9～1.1g/L；对氨基苯磺酸盐4～6g/L；磷酸二氢锌2～4g/L。

【技术特征摘要】
1.一种钢板用水性无铬快速成膜处理液，其特征在于，处理液的成分包括：硫脲6～10g/L；丁二酸15～17g/L；硼酸0.9～1.1g/L；对氨基苯磺酸盐4～6g/L；磷酸二氢锌2～4g/L。2.根据权利要求1所述的钢板用水性无铬快速成膜处理液的制备方法，其特征在于，包括以下步骤：向水中加入对氨基苯磺酸盐并搅拌均匀，然后加入丁二酸并搅拌均匀，再加入硫脲并...

【专利技术属性】
技术研发人员：王雷，岳重祥，李化龙，李慧，
申请(专利权)人：江苏省沙钢钢铁研究院有限公司，
类型：发明
国别省市：江苏,32