Ultra high performance concrete and the preparation method of the invention provides a coarse aggregate containing basalt, consists of cementitious material, aggregate, water, polycarboxylate superplasticizer and steel fiber; the method of the raw materials according to a certain order mixed after taking natural curing to obtain the product. The basalt gravel as coarse aggregate are incorporated into the ultra high performance concrete, can effectively inhibit the ultra high performance concrete shrinkage, the strength decrease under the condition of small, can greatly reduce the production cost of the ultra high performance concrete, and the maintenance method is simple and is convenient for practical use.
【技术实现步骤摘要】
一种含玄武岩粗骨料的超高性能混凝土及其制备方法
本专利技术属于建筑材料
，尤其涉及一种含玄武岩粗骨料的超高性能混凝土及其制备方法。
技术介绍
超高性能混凝土(UltraHighPerformanceConcrete，UHPC)因具有超高强度、高工作性能和高耐久性，相比普通混凝土而言，相同截面下具有更高的承载能力和更好的耐久性，从而可以减小结构构件的截面尺寸，减轻了结构自身的重量，增大了建筑物的空间，使得建筑朝着高层化、轻质化、大跨化和高耐久性方面发展，这也是建筑结构未来发展的方向。UHPC除了具有上述三种优秀的性能外，还具有优越的抗渗、抗爆、抗冲击的性能，可用于核电站和重要军事建筑物等对抗渗和抗爆具有严格的要求的建筑物。活性粉末混凝土(ReactivePowderConcrete，RPC)是以水泥和矿物等活性粉末材料、细骨料、外加剂、高强度钢纤维等原料生产而成的超高强增韧混凝土，其通过提高组分的细度和活性来提高材料的致密度，达到提高材料性能的目的。此外，由于RPC胶凝材料含量高，去除了粗骨料，养护制度要求采用高温养护，生产成本高，同时自收缩现象严重，导致其在...
【技术保护点】
一种含玄武岩粗骨料的超高性能混凝土，其特征在于：包括下述配比的原料：胶凝材料：850～950kg/m
【技术特征摘要】
1.一种含玄武岩粗骨料的超高性能混凝土，其特征在于：包括下述配比的原料：胶凝材料：850～950kg/m3，其中包括：水泥：595～665kg/m3，硅灰：85～95kg/m3，粉煤灰：170～190kg/m3；骨料：包括细骨料：480～530kg/m3，粗骨料：720～800kg/m3；水：153～171kg/m3；聚羧酸高效减水剂：21.25～23.75kg/m3；钢纤维：157kg/m3；所述水与胶凝材料的水胶比为0.18～0.2；所述的聚羧酸高效减水剂掺量为胶凝材料质量的2.5％。2.如权利要求1所述的含玄武岩粗骨料的超高性能混凝土，其特征在于：所述的水泥为强度等级为52.5级或52.5R级的硅酸盐水泥或者普通硅酸盐水泥；所述的硅灰要求二氧化硅含量不低于95％，平均粒径为0.2μm。3.如权利要求1所述的含玄武岩粗骨料的超高性能混凝土，其特征在于：所述的细骨料为机制石英砂，SiO2的含量≥97％，其粒径为0.4～0.7mm，平均粒径为0.55mm，Ⅱ区中砂；所述的粗骨料为玄武岩，由粒径范围5～10mm和10～20mm的两种材料按质量比小粒径：大粒径＝3:7...
【专利技术属性】
技术研发人员：徐礼华，吴方红，池寅，余敏，卢秋如，程鹏，
申请(专利权)人：武汉大学，
类型：发明
国别省市：湖北,42