本发明专利技术公开了一种贝壳粉表面修饰制备纳米助磨剂的方法，助磨剂配方是质量分数0.2‑0.4%贝壳粉，质量分数0.002‑0.004%修饰剂。制备方法是将贝壳水洗、破碎制备贝壳载体，将修饰剂液体滴加到贝壳载体上，混合均匀，密封保存。优点：充分发挥天然纳米材料贝壳和修饰剂的各自优点，实现分子层面优化设计，满足工程对水泥使用性能的要求。具有利废、节能、增强、适用范围广、生产成本低的绿色纳米功能助磨剂。

Surface grinding nanometer powder grinding agent for shell powder

The invention discloses a method for preparing nanometer surface modification of shell powder grinding agent, grinding agent is 0.2 mass fraction of 0.4% shell powder, the mass fraction of 0.002 0.004% modifier. The preparation method is that the shell is washed and broken to prepare shell carrier, and the modifier liquid is added to the shell carrier to be mixed evenly and sealed to preserve. Advantages: give full play to the advantages of natural nano materials, shells and modifiers, realize the optimization design at the molecular level, and meet the requirements of engineering for the performance of cement. The utility model has the advantages of waste, energy saving, enhancement, wide application range and low production cost, and is a green nanometer grinding aid.

【技术实现步骤摘要】
一种贝壳粉表面修饰纳米助磨剂
本专利技术属于利用废弃物生产助磨剂新技术，具体涉及一种贝壳粉表面修饰纳米助磨剂的配方和制备方法。
技术介绍
贝壳是海洋贝类水产品加工后的副产物，来源丰富。开发利用贝壳资源，变废为宝，减少对环境的负荷。贝壳由无机碳酸钙和有机基体组成的复合矿物质，天然的纳米生物材料。我国水泥产量全球第一，高速发展造成资源和能源消耗大，噪声高、废气、粉尘污染物排放量多。节能、降耗、减排、提质增效是水泥可持续发展的供给侧改革之路。每生产1吨水泥需要粉磨各种物料3t左右，使粉磨电耗约占水泥生产总电耗的60~70%。助磨剂是在水泥粉磨时加入的起助磨作用而不损害水泥性能的外加剂，掺量规定不超过水泥质量的0.5%。具有消除细粉的粘附和聚集现象，降低单位粉磨电耗，提高产量的作用。助磨剂种类有液体、固体和气体三种形态。液体助磨剂目前应用广泛，效果好。缺点是价格较高，来源短缺，操作不便捷，影响水泥使用安全性能。计量精度不准确，掺量少，粉体粗。掺量多，水泥细度过细，水泥标准稠度用水量增加，水泥强度降低，凝结时间延长。磨机进料液体粘度大，主要吸附在石膏等易磨性好的材料表面上，对熟料润湿和吸附作用本文档来自技高网...

【技术保护点】
一种贝壳粉表面修饰纳米助磨剂，其特征在于：由下述重量配比的原料制成：贝壳粉0.2‑0.4份；修饰剂0.002‑0.004份。

【技术特征摘要】
1.一种贝壳粉表面修饰纳米助磨剂，其特征在于：由下述重量配比的原料制成：贝壳粉0.2-0.4份；修饰剂0.002-0.004份。2.如权利要求1所述的一种贝壳粉表面修饰纳米助磨剂，其特征在于，由下述重量配比的原料制成：贝壳粉0.2份；有机硅修饰剂0.002份。3.根据权利要求1-2...