一种飞秒激光直写具有宽光谱荧光特性的PbS量子点掺杂玻璃及其制备方法技术
Femtosecond laser direct writing PbS quantum point doped glass with wide spectral fluorescence characteristic and preparation method thereof
The invention relates to a femtosecond laser PbS quantum dot doped glass and its preparation method has wide spectral fluorescence characteristics of direct writing, the quantum dot luminescence glass including glass substrate and which is obtained by focusing femtosecond laser irradiation photoluminescence part. The prepared luminescent glass doped with sulfur and lead, by focusing femtosecond laser irradiation, laser irradiation induced precipitation in the area of PbS quantum dots, the region has the photoluminescence properties. The high light intensity of the emitting region, covering 860 of the 1700 nm wide near infrared band, with applications in the near infrared wide spectrum light source etc..
【技术实现步骤摘要】
一种飞秒激光直写具有宽光谱荧光特性的PbS量子点掺杂玻璃及其制备方法
本专利技术涉及一种发光玻璃，具体涉及一种飞秒激光直写具有宽光谱荧光特性的PbS量子点掺杂玻璃及其制备方法。
技术介绍
近年来发展的硫化铅、硒化铅量子点材料由于其量子限域效应、尺寸效应和表面效应等特点，展现出许多独特的光学特性，最显著的是其发光光谱可覆盖很宽的近红外波段，因此其在红外探测和近红外荧光应用方面备受关注。目前所报道的研究量子点掺杂玻璃主要采用热处理法制备，即将制备好的玻璃基体在高于玻璃转变点的某一温度范围内保温一段时间。但是采用热处理法制备量子点掺杂玻璃所需温度较高，时间较长，能源消耗大。同时，采用热处理方法所制备的量子点掺杂玻璃，玻璃基质中量子点的粒径分布范围受热处理温度与时间的影响，一般情况下，量子点掺杂玻璃的荧光峰半高宽较窄，难以制备具有宽荧光光谱特性的量子点掺杂玻璃。此外，采用热处理法所制备的量子点掺杂玻璃中，量子点在玻璃基质中均匀分布，无法调控量子点在玻璃基质中的空间分布，难以通过此方法制备量子点掺杂玻璃的光功能器件。因此，开发一种新型的玻璃基质中量子点可控制备方法，实现玻璃...
【技术保护点】
一种飞秒激光直写具有宽光谱荧光特性的PbS量子点掺杂玻璃，其特征在于，所述发光玻璃包括未受激光辐照的玻璃基体和其中飞秒激光直写的发光区域。
【技术特征摘要】
1.一种飞秒激光直写具有宽光谱荧光特性的PbS量子点掺杂玻璃，其特征在于，所述发光玻璃包括未受激光辐照的玻璃基体和其中飞秒激光直写的发光区域。2.根据权利要求1所述的飞秒激光直写具有宽光谱荧光特性的PbS量子点掺杂玻璃的制备方法，其特征在于，包括以下步骤：1)选取合适的玻璃；2)将飞秒激光聚焦并辐照步骤1)所述的玻璃中，使用飞秒激光写入一个立体区域，得到飞秒激光辐照的光致发光区域；3)将步骤2)所制的玻璃进行高温处理。3.根据权利要求2所述的制备方法，其特征在于,步骤1)所述的玻璃含有硫和铅，所述玻璃经过高温热处理在玻璃基质中析出硫化铅量子点。4.根据权利要求2所述的制备方法，其特征在于，步骤2)所述飞秒激光的辐照方...
【专利技术属性】
技术研发人员：刘超，胡煜洲，赵志永，韩建军，
申请(专利权)人：武汉理工大学，
类型：发明
国别省市：湖北,42