本发明专利技术提供一种新型玻璃及其生产工艺，涉及玻璃生产技术领域，玻璃是由以下重量份的原料制成：石英砂50‑70份、纯碱15‑20份、方解石2‑8份、钠长石2‑8份、石灰石2‑6份、高岭土3‑6份、白云石1‑6份、氧化物澄清剂0.2‑0.6份，生产工艺包括以下步骤：(1)原料预加工、(2)配合料制备、(3)熔料、(4)成型、(5)退火；本发明专利技术解决了现有玻璃及其生产工艺存在着缺少粉碎和干燥处理环节、对原料配方和工艺参数不能够调整和控制、制作的玻璃品质差的问题。

Novel glass and production process thereof

The present invention provides a new type of glass and its production process and relates to the technical field of glass production, glass is made from the following raw materials in weight portion: 50 quartz sand 70, soda ash 15 20 copies, 8 copies, 2 calcite albite 2 8 copies, 6 copies of 2 limestone and kaolin 3 6 1, 6, dolomite 0.2 oxide clarifying agent 0.6, the production process includes the following steps: (1) pre processing of raw materials, (2) batch preparation, (3), (4) melt molding, annealing (5); the invention solves the lack of glass and its production process crushing and drying process, can adjust and control problems, poor quality of the glass making raw material formula and process parameters.

【技术实现步骤摘要】
一种新型玻璃及其生产工艺
本专利技术属于玻璃生产
，具体涉及一种新型玻璃及其生产工艺。
技术介绍
玻璃的通透感好、无污染、时尚性强、造型丰富、应用广泛、成本低廉。玻璃的模具成型尺寸精确，可以制造轻薄型产品，而且颜色丰富多变、工艺精美。2016年1月20日公告的中国专利文献一种瓷白玻璃及其生产工艺(授权公告号CN103482870B)，该生产工艺包括如下步骤：(1)配合料制备；(2)熔化：将配合料和碎玻璃投入窑炉熔化；(3)成型：利用玻璃成型设备进行成型加工；(4)退火：利用退火窑退火。所述瓷白玻璃配方由如下按重量百分比计的原料组成：60-90％配合料，10-40％碎玻璃；所述配合料包括如下按重量份比例计的组分：50-60份的石英砂，13.5-16份的纯碱，10-12份的氢氧化铝，9-11份的氟硅酸钠，5-7份的萤石，0-1.5份的硫酸钡，0.5-2份的硝酸钠，0-3份的方解石，0.3-0.7份的复合澄清剂。该专利技术通过对原料配方、工艺参数的精细调整和控制，得到具有高白瓷器外观效果的瓷白玻璃。但该专利技术中的玻璃原料很多是呈块状且潮湿的，需要粉碎和干燥处理，不然原料混合不均匀，本文档来自技高网...

【技术保护点】
一种新型玻璃，其特征在于，其是由以下重量份的原料制成：

【技术特征摘要】
1.一种新型玻璃，其特征在于，其是由以下重量份的原料制成：2.根据权利要求1所述的新型玻璃，其特征在于，其是由以下重量份的原料制成：3.根据权利要求2所述的新型玻璃，其特征在于，其是由以下重量份的原料制成：4.根据权利要求1所述的新型玻璃，其特征在于：所述氧化物澄清剂为白砒或硝酸盐。5.根据权利要求4所述的新型玻璃，其特征在于：所述氧化物澄清剂为白砒。6.一种如权利要求1所述的新型玻璃的生产工艺，其特征在于，包括以下步骤：(1)原料预加工：将块状原料粉碎，使潮湿原料干燥；(2)配合料制备：将原料按照玻璃的重量份的原料...