一种堇青石透明耐磨釉及其制备方法技术

本发明专利技术公开了一种堇青石透明耐磨釉，其组分按以下重量百分比含有：高岭土50～55％、滑石25～32％、钠长石2～8％、含钙化合物5～8％、硼酸4～8％、碳酸锂1～5％、余量为石英。本发明专利技术还公开了上述堇青石透明耐磨釉的制备方法。本发明专利技术提高传统陶瓷釉面砖的耐磨性以及原料的利用率，且制备过程中不需要引入成核剂，烧成温度低，烧成工业简单，不会因为成核剂的引入而导致釉面着色。

Cordierite transparent wear-resistant glaze and preparation method thereof

The invention discloses a cordierite transparent wear-resistant glaze and its components by the following weight percentage: 50 to 55%, containing kaolin, talc 25 ~ 32%, 2 ~ 8%, sodium feldspar calcium compounds 5 ~ 8%, 4 ~ 8% boric acid and lithium carbonate from 1 to 5%, the balance of quartz. The invention also discloses the preparation method of the cordierite transparent wear-resistant glaze. The invention improves the traditional ceramic tile abrasion resistance and the utilization rate of raw materials, and the preparation process does not require the introduction of nucleating agent, low sintering temperature, sintering industry, not because of the introduction of nucleating agent and lead glaze coloring.

【技术实现步骤摘要】
一种堇青石透明耐磨釉及其制备方法
本专利技术涉及釉料及其制备方法，特别涉及一种堇青石透明耐磨釉及其制备方法。
技术介绍
堇青石分子式为2MgO·2Al2O3·5SiO2，它有三种晶型，低温以μ-堇青石形式存在，也被称作镁铝硅酸盐，属于菱形晶系；950℃结晶形成β-堇青石，属于斜方晶系，是自然界中存在的一种形式；高温下以α-堇青石形式存在，它属于六角片状。堇青石由于其具有热膨胀系数低、热导率小、抗热震性好、介电常数低、介电损耗小等等特点，被广泛的应用于汽车尾气排放、泡沫陶瓷、蜂窝陶瓷、涡轮发动机以及工业热转换器等等各个方面。由于低膨胀系数的堇青石晶粒均匀的分散在高膨胀系数釉面会产生预压应力，对釉面起到增强增韧提高硬度的作用，再因其与玻璃有相似的折射率，对制得透明结晶釉有显著的优势。传统釉面砖由于其釉面耐磨损性差，对釉面砖的利用率低，相对的对能源资源的消耗量大，限制了釉面砖的快速发展，近些年抛光砖有突破釉面砖发展的优势，但由于其难以清洁、颜色单一成为了难以逾越的鸿沟。因此，制备一种耐磨性高，且不影响釉面颜色、光泽度的结晶釉才是唯一的出路。专利号104829267A一种高耐磨釉中彩陶瓷釉面本文档来自技高网...

【技术保护点】
一种堇青石透明耐磨釉，其特征在于，其组分按以下重量百分比含有：

【技术特征摘要】
1.一种堇青石透明耐磨釉，其特征在于，其组分按以下重量百分比含有：2.权利要求1所述的堇青石透明耐磨釉的制备方法，其特征在于，包括以下步骤：(1)按权利要求1所述的组分称取原料，经球磨混合、干燥过筛，随后将粉料在1400℃～1450℃保温1.5h～2h后淬冷制成熔块；(2)将步骤(1)得到的熔块球磨、干燥过筛，得到熔块粉；(3)在步骤(2)得到的熔块粉中加入熔块粉的5wt％～8wt％的高岭土，装入球磨罐内进行湿法球磨混合0.5h～1h，得到陶瓷浆料；(4)将步骤(3)得到的陶瓷浆料施釉于素烧过的坯体上，自然风干后，升温至1100～1250℃并保温0.5h～1h，获得单相堇青石耐磨釉。3.根据权利要求2所述的堇青石透明耐磨...

【专利技术属性】
技术研发人员：吕明，陈鹏，彭诚，饶平根，吴建青，
申请(专利权)人：华南理工大学，
类型：发明
国别省市：广东,44