The invention discloses a cement clinker and its preparation method, the cement clinker is prepared from the following components in parts by weight: two calcium silicate 30 45, three 35 50 calcium silicate, ferritealuminate four calcium 8 20, 5 15 gehlenite, carboxymethyl 2.5 cellulose 6, Magnesium Oxide 1 6 copies, 6 copies of 2 calcium oxide, iron oxide 1 3 copies, 8 copies of 4 silica. Cement clinker in the invention is composed of the composition of raw materials and reasonable collocation, and has the advantages of easily obtained raw materials, simple preparation method, which mainly joined Magnesium Oxide, carboxymethyl cellulose, calcium oxide and iron oxide, so that the mechanical strength of cement clinker is greatly enhanced, while reducing the calcination process energy consumption.
【技术实现步骤摘要】
一种水泥熟料及其制备方法
本专利技术涉及建筑材料
，具体涉及一种水泥熟料及其制备方法。
技术介绍
随着经济社会的不断发展，人们对各种大型工程的质量要求越来越高，建筑材料是保障工程质量的重要一环，众所周知，水泥是建筑材料的一种，其使用性能也直接影响工程质量，由于现有水泥熟料在煅烧过程中具有耗能大，其机械强度低，因而大大影响水泥的使用效果。
技术实现思路
本专利技术的目的在于提供一种水泥熟料及其制备方法，其具有原料简单易得、制备方法简单且使用性能优良等优点。为实现上述目的，本专利技术提供如下技术方案：一种水泥熟料，它是由以下重量份数的组分制成：硅酸二钙30-45份，硅酸三钙35-50份，铁铝酸四钙8-20份，钙铝黄长石5-15份，羧甲基纤维素2.5-6份，氧化镁1-6份，氧化钙2-6份，氧化铁1-3份，二氧化硅4-8份。优选地，所述水泥熟料由以下重量份数的组分制成：硅酸二钙36份，硅酸三钙48份，铁铝酸四钙14份，钙铝黄长石11份，羧甲基纤维素3.5份，氧化镁2份，氧化钙3份，氧化铁1.6份，二氧化硅5份。优选地，所述水泥熟料由以下重量份数的组分制成：硅酸二钙32份...
【技术保护点】
一种水泥熟料，其特征在于，它是由以下重量份数的组分制成：硅酸二钙30‑45份，硅酸三钙35‑50份，铁铝酸四钙8‑20份，钙铝黄长石5‑15份，羧甲基纤维素2.5‑6份，氧化镁1‑6份，氧化钙2‑6份，氧化铁1‑3份，二氧化硅4‑8份。
【技术特征摘要】
1.一种水泥熟料，其特征在于，它是由以下重量份数的组分制成：硅酸二钙30-45份，硅酸三钙35-50份，铁铝酸四钙8-20份，钙铝黄长石5-15份，羧甲基纤维素2.5-6份，氧化镁1-6份，氧化钙2-6份，氧化铁1-3份，二氧化硅4-8份。2.根据权利要求1所述的一种水泥熟料，其特征在于：所述水泥熟料由以下重量份数的组分制成：硅酸二钙36份，硅酸三钙48份，铁铝酸四钙14份，钙铝黄长石11份，羧甲基纤维素3.5份，氧化镁2份，氧化钙3份，氧化铁1.6份，二氧化硅5份。3.根据权利要求1所述的一种水泥熟料，其特征在于：所述水泥熟料由以下重量份数的组分制成：硅酸二钙32份，硅酸三钙42份，铁铝酸四钙13份，钙铝黄长石8份，羧甲基纤...
【专利技术属性】
技术研发人员：武为冬，王召，
申请(专利权)人：安徽珍珠水泥集团股份有限公司，
类型：发明
国别省市：安徽,34