The invention discloses a micro expansion toughened cement slurry and its preparation method, the micro expansion toughened cement slurry comprises the following components in part by weight: 100 portions of cement, latex from 8 to 15, 1 to 2 portions of filtrate reducer, drag reduction agent 1 ~ 1.5, 1 ~ 2 early strength agent a swelling agent 2 ~ 4, defoaming agent 0.2 ~ 0.5 copies, 40 copies of water. The micro expansion toughness cement slurry has very low filtration loss, and has the characteristics of good toughness, good rheology, volume shrinkage, high early strength and so on. The micro expansion is applied to toughen the cement slurry. The construction is simple, the technical superiority and the environmental protection superiority are remarkable, and the on-site cementing quality is excellent.
【技术实现步骤摘要】
一种微膨胀增韧水泥浆及其制备方法
本专利技术涉及钻井固井工程领域，具体涉及了一种微膨胀增韧水泥浆及其制备方法。
技术介绍
河南油田老区由于老井套管损坏、老井报废等导致油水井网布局不合理，严重影响了剩余油的开采。利用套管开窗侧钻工艺技术对报废井、套损井、低效井进行开窗侧钻，可以完善注采井网，提高采收率，实现了综合经济效益的提升。为满足后期射孔等技术要求，目前河南油田开窗井选用Φ95.25mm非标套管作为完井生产套管；而套管与井壁的环空间隙较小(环空间隙仅11mm)，施工排量小固井顶替效率低，排量大循环压力高，容易憋漏地层；同时对固井水泥石韧性要求很高，导致固井质量难以保证。《中国石油学会2005东部油田钻井新技术研讨会论文集》中《韧性水泥浆体系研究与应用》(尹学源，2005)一文公开了一种韧性水泥浆体系，该水泥浆体系的组成包括：水泥700g、胶乳105g、稳定剂(7+7)g、分散剂10g、CCF-200L7g、CCA9g、消泡剂2g、混合水310g。该水泥浆体系是通过在常规水泥浆中掺入增韧材料后改善水泥石的韧性性能(弹性模量)、抗压强度以及加入相应的降失水剂从而形成...
【技术保护点】
一种微膨胀增韧水泥浆，其特征在于：由以下重量份的组分组成：油井水泥100份，胶乳8～15份，降失水剂1～2份，减阻剂1～1.5份，早强剂1～2份，膨胀剂2～4份，消泡剂0.2～0.5份，水40份。
【技术特征摘要】
1.一种微膨胀增韧水泥浆，其特征在于：由以下重量份的组分组成：油井水泥100份，胶乳8～15份，降失水剂1～2份，减阻剂1～1.5份，早强剂1～2份，膨胀剂2～4份，消泡剂0.2～0.5份，水40份。2.根据权利要求1所述的微膨胀增韧水泥浆，其特征在于：由以下重量份的组分组成：油井水泥100份，胶乳10份，降失水剂1.5份，减阻剂1份，早强剂1.5份，膨胀剂2份，消泡剂0.2份，水40份。3.一种如权利要求1所述的微膨胀增韧水泥浆的制备方法，其特征在于：包括以下步骤：1)取配方量的油井水泥、降失水剂、减阻剂、早强剂、膨胀剂混合均匀，得混合物A；取配方量的胶乳、消泡剂加入水中混合，得混合物B；2)将步骤1)所得的混合物A和混合物B混合，即得。4.根据权利要求3所述的微膨胀增韧水泥浆的制备方法，其特征在于：步骤1)中，在制备混合物A时，所述混合为在室温下干混，干混时间为3～5m...
【专利技术属性】
技术研发人员：郭进忠，赵林，王海娟，曾欣，陈平，仝继昌，