The invention belongs to the field of metal rust, is a kind of metal anti rust paper, it consists of the following parts by weight of raw materials: three benzo triazole 4 ~ 8, 35 ~ 40 ethanol, two butyl 10 adipic acid ~ 15, four ~ 35 five ethylene amine 30, triethanolamine 5 ~ 8, the amount of calcium sulfonate; preparation. The materials are mixed evenly made of antirust liquid, the coating on the front and on the back of the neutral paper, neutral paper coated with moisture-proof agent, when in use, the front and back of the metal contact paper, paper can contact with the atmosphere; the invention has the advantages of simple formulation, convenient preparation, use quickly, of steel brass, bronze, brass, copper, aluminum, silicon, anodic oxidation, cadmium plating, zinc has a good anti-corrosion effect.
【技术实现步骤摘要】
一种金属防锈纸
本专利技术属于金属防锈
，特别是一种金属防锈纸。
技术介绍
大多数的活泼金属或半活泼金属制品及其合金制品均存在锈蚀，在使用或储存过程中如何使金属防锈成为一大难题，目前市面上也有一些防锈液、防锈纸产品，然而这些产品大多数都只能保护一种或两种金属制品的防锈，一般来说，几乎所有的工厂都同时存在多种需要防锈的产品，这样，在公司采购时就需要分门别类的购买好多种防锈产品，给公司的采购带来麻烦，同时也带来经济上的负担，因此，研发一种金属防锈纸十分必要。
技术实现思路
本专利技术的目的就是要解决目前市面上的防锈纸、防锈液均功能较为单一，只能解决一两种金属的防锈，给大多数公司的采购带来困扰的问题，提供一种金属防锈纸。本专利技术的一种金属防锈纸，由下述重量份原料组成：苯骈三唑4～8乙醇35～40己二酸二丁酯10～15四乙烯五胺30～35三乙醇胺5～8石油磺酸钙适量；制备时，将上述物料混合搅拌均匀制成防锈液，将其涂覆在中性纸的正面，然后在中性纸的背面涂上防潮剂，使用时，将纸的正面与金属接触，纸的背面与大气接触即可。本专利技术的一种金属防锈纸，其优选配方由下述重量份原料组成：苯骈三唑6乙醇38己二酸二丁酯12四乙烯五胺33三乙醇胺6石油磺酸钙适量。本专利技术配方简单，制备方便，使用快捷迅速，对钢、黄铜、青铜、硅黄铜、紫铜、铝、阳极氧化、镀镉、镀锌等均有良好的防绣效果，方便了大多数厂家的使用需求，为客户的采购流程带来极大的方便，节省了企业的人力、物力、财力，值得广泛推广。具体实施方式实施例1本专利技术的一种金属防锈纸，由下述重量份原料组成：苯骈三唑6乙醇38己二酸...
【技术保护点】
一种金属防锈纸，其特征在于由下述重量份原料组成：苯骈三唑 4～8 乙醇 35～40己二酸二丁酯 10～15 四乙烯五胺 30～35三乙醇胺 5～8 石油磺酸钙 适量；制备时，将上述物料混合搅拌均匀制成防锈液，将其涂覆在中性纸的正面，然后在中性纸的背面涂上防潮剂，使用时，将纸的正面与金属接触，纸的背面与大气接触即可。
【技术特征摘要】
1.一种金属防锈纸，其特征在于由下述重量份原料组成：苯骈三唑4～8乙醇35～40己二酸二丁酯10～15四乙烯五胺30～35三乙醇胺5～8石油磺酸钙适量...