The invention belongs to the technical field of adhesives, is a kind of high temperature resistant metal adhesives, which consists of the weight of raw materials: 30-40 bauxite, kaolin 10-20, 25-35 phosphate, silicate sol 3-8, aluminum hydroxide 3-6, water 8-12; during the preparation of the aluminum hydroxide mixed with water, adding phosphoric acid, heated under stirring conditions and get the clear liquid, cooling after mixing with bauxite, kaolin, silica sol, stirring into a thick paste, namely; the invention of easily obtained raw materials, simple process, strong adhesion, easy to use, can be used in the condition of high temperature, especially suitable for the repair of heated metal pipes and metal fracture condition the model can be used for boiler pipe grinding cracks or adhesive wear.
【技术实现步骤摘要】
一种耐高温金属黏合剂
本专利技术属于胶粘剂
，具体是一种耐高温金属黏合剂。
技术介绍
锅炉是工业生产中必不可少的设备，锅炉管道是一种耐高温、高压设备，但是由于其长期处于高温高压状态，难免会出现管道磨穿或者裂缝，而一旦发生此类事故，首先要确保生产能够正常进行，维持到一批产品下线才能进行维修，这样就需要一种能够在高温下进行紧急修补的金属胶粘剂，以应付突发状况，保证生产正常进行，而目前普通的胶粘剂都无法在高温下使用。因此，研发一种高温专用金属黏合剂，是锅炉能够正常运行的重要保障。
技术实现思路
本专利技术的目的就是针对目前普通的胶粘剂不能在高温下使用，导致锅炉管道等在高温高压下使用的设备在生产中遇到裂缝或管道磨穿等问题无法及时维修，保障生产正常进行的问题，而提供一种耐高温金属黏合剂。本专利技术的一种耐高温金属黏合剂,由下述重量份原料组成：高铝矾土30-40高岭土10-20磷酸25-35硅酸溶胶3-8氢氧化铝3-6水8-12；制备时，先将氢氧化铝与水混合，再加入磷酸，在搅拌状态下加热，得到清澈的液体，冷却后与高铝矾土、高岭土、硅酸溶胶混合，搅拌成粘稠膏状，即得。本专利技...
【技术保护点】
一种耐高温金属黏合剂,其特征在于由下述重量份原料组成：高铝矾土 30‑40 高岭土 10‑20磷酸 25‑35 硅酸溶胶 3‑8氢氧化铝 3‑6 水 8‑12；制备时，先将氢氧化铝与水混合，再加入磷酸，在搅拌状态下加热，得到清澈的液体，冷却后与高铝矾土、高岭土、硅酸溶胶混合，搅拌成粘稠膏状，即得。
【技术特征摘要】
1.一种耐高温金属黏合剂,其特征在于由下述重量份原料组成：高铝矾土30-40高岭土10-20磷酸25-35硅酸溶胶3-8氢氧化铝3-6水8-1...