The invention is a woven bag to a formula of strength and toughness is good, by weight portion of the raw materials made of polystyrene: acid 90; anti ageing agent 1.5 2.5; 1 nano sulfobetaine 2; coupling agent 1 1.5; 0.3 antioxidant 0.6; nano calcium carbonate 10 15 A; aldacide 8 10; 20 25 metallocene polyethylene; polyethylene wax 1.3 1.6; 3 ethylene methyl acrylate copolymer 3.5; citric acid three butyl 1.5 2; 0.5 turpentine 0.9; ultraviolet absorbent 5 8; 1 2 titanium dioxide 0.02; Ultramarine 0.04; fine aluminum powder 0.1 0.5; made by the invention of plastic woven bags of sunscreen performance, anti-aging ability, service life increased, tensile properties can be enhanced, and the color is more white, with good economic benefits.
【技术实现步骤摘要】
一种强度与韧性俱佳的编织袋配方
本专利技术涉及塑料编织袋生产
,尤其涉及一种强度与韧性俱佳的编织袋配方。
技术介绍
塑料编织袋是一种应用十分广泛的包装带,常见产品有饲料编织袋、腻子粉编织袋、尿素编织袋、蔬菜网眼袋、水果网眼袋、大米编织袋、面粉编织袋、玉米编织袋等,其主要生产工艺是利用塑料原料经塑制造粒、扁丝拉伸、圆织布基、涂膜、印刷、切割、缝纫得到产品,最后打包出厂。传统的塑料编织袋易老化,使用寿命短,抗紫外线性能差,拉伸力低,使得装载的物品极易产生腐败变质,货物挪移途中因编织袋中途撕裂破损导致货物散落满地难以归整,因此,急需提高塑料编织袋的防晒性能,延长其寿命和提高拉伸性能,而在塑料编织袋的生产过程中,塑料编织袋原料配方的性能对编织塑料袋的性能起到决定性影响,目前的编织塑料袋存在表面不够白的现象,对所包装的物品的销售造成不良影响。
技术实现思路
本专利技术旨在解决现有技术的不足,而提供一种强度与韧性俱佳的编织袋配方。本专利技术为实现上述目的,采用以下技术方案:一种强度与韧性俱佳的编织袋配方,其特征在于,由下列重量份的原料制作而成:聚苯二酸90份;防老化剂1.5-2.5份;纳米磺酸甜菜碱1-2份;偶联剂1-1.5份;抗氧剂0.3-0.6份;纳米碳酸钙10-15份;聚氧化甲烯8-10份;茂金属聚乙烯20-25份;聚乙烯蜡1.3-1.6份;乙烯-丙烯酸甲酯共聚物3.0-3.5份;柠檬酸三丁酯1.5-2份;松节油0.5-0.9份;紫外线吸收剂5-8份;钛白粉1-2份;群青0.02-0.04份;细粒铝银粉0.1-0.5份。本专利技术的有益效果是:用本专利技术制成 ...
【技术保护点】
一种强度与韧性俱佳的编织袋配方,其特征在于,由下列重量份的原料制作而成: 聚苯二酸90份; 防老化剂1.5‑2.5份; 纳米磺酸甜菜碱1‑2份; 偶联剂1‑1.5份; 抗氧剂0.3‑0.6份; 纳米碳酸钙10‑15份; 聚氧化甲烯8‑10份; 茂金属聚乙烯20‑25份; 聚乙烯蜡1.3‑1.6份; 乙烯‑丙烯酸甲酯共聚物3.0‑3.5份; 柠檬酸三丁酯1.5‑2份; 松节油0.5‑0.9份; 紫外线吸收剂5‑8份; 钛白粉1‑2份; 群青0.02‑0.04份; 细粒铝银粉0.1‑0.5份。
【技术特征摘要】
1.一种强度与韧性俱佳的编织袋配方,其特征在于,由下列重量份的原料制作而成:聚苯二酸90份;防老化剂1.5-2.5份;纳米磺酸甜菜碱1-2份;偶联剂1-1.5份;抗氧剂0.3-0.6份;纳米碳酸钙10-15份;聚氧化甲烯8-10份;...