With the process of 165ksi high strength drill pipe coating for oil drilling, the drill into the line, clean, then use hot cleaning furnace, remove the inner surface of drill pipe, oil pipe wall impurities; then the surface by sand blasting machine; and inner wall of the drill pipe for advanced primer spray coating, preliminary curing, and then after spraying the paint is heated to 80-120 deg.c solidification; after curing of leak detection, qualified for zero leakage; the automatic external anti-corrosion spray and automatic marking, packaging and warehousing. The invention adopts a special primer and topcoat formula, so that the 165ksi high strength drill pipe inner coating has excellent chemical resistance performance and corrosion resistance, and can be suitable for containing H
【技术实现步骤摘要】
石油开采用165ksi高强度钻杆内涂层工艺
本专利技术涉及管材防腐，尤其涉及一种石油开采用165ksi高强度钻杆内涂层工艺。
技术介绍
对于165ksi高强度钻杆，其内涂层质量要求很高。但现有技术的内涂层工艺，尚不能满足这一要求。主要原因是涂料不能满足高强度钻杆的要求。有必要开发一种可以适用于温度≤200℃，含H2S、CO2等多种腐蚀介质的环境中的涂料，用于165ksi高强度钻杆中。
技术实现思路
本专利技术的目的，就是为了解决上述问题，提供一种石油开采用165ksi高强度钻杆内涂层工艺。为了达到上述目的，本专利技术采用了以下技术方案：一种石油开采用165ksi高强度钻杆内涂层工艺，包括钻杆入线、清洁，还包括以下步骤：A、使用热清洁炉将钻杆内表面的各种油污、杂质进行碳化；B、使用喷砂机对钻杆的内壁进行表面处理，将碳化的各种油污、杂质脱除，检查内壁表面处理合格后，将内壁吹扫干净；C、对钻杆的内壁先进行底漆喷涂，初步固化，然后进行面漆喷涂后加热到80-120℃固化；D、固化后进行漏点检测，无漏点为合格；E、对钻杆的外壁进行全自动外防腐喷涂；F、全自动喷标；G、打包入库；所...
【技术保护点】
一种石油开采用165ksi高强度钻杆内涂层工艺，包括钻杆入线、清洁，其特征在于，还包括以下步骤：A、使用热清洁炉将钻杆内表面的各种油污、杂质进行碳化；B、使用喷砂机对钻杆的内壁进行表面处理，将碳化的各种油污、杂质脱除，检查内壁表面处理合格后，将内壁吹扫干净；C、对钻杆的内壁先进行底漆喷涂，初步固化，然后进行面漆喷涂后加热到80‑120℃固化；D、固化后进行漏点检测，无漏点为合格；E、对钻杆的外壁进行全自动外防腐喷涂；F、全自动喷标；G、打包入库；所述底漆由下列重量份含量的物质配制而成：
【技术特征摘要】
1.一种石油开采用165ksi高强度钻杆内涂层工艺，包括钻杆入线、清洁，其特征在于，还包括以下步骤：A、使用热清洁炉将钻杆内表面的各种油污、杂质进行碳化；B、使用喷砂机对钻杆的内壁进行表面处理，将碳化的各种油污、杂质脱除，检查内壁表面处理合格后，将内壁吹扫干净；C、对钻杆的内壁先进行底漆喷涂，初步固化，然后进行面漆喷涂后加热到80-120℃固化；D、固化后进行漏点检测，无漏点为合格；E、对钻杆的外壁进行全自动外防腐喷涂；F、全自动喷标；G、打包入库；所述底漆由下列重量份含量的物质配制而成：所述面漆由下列重量份含量的物质配制而成：2.如权利要求1所述的石油开采用165ksi高强度钻杆内涂层工艺，其特征在于：所述基体树脂选自...
【专利技术属性】
技术研发人员：郑红刚，宋卫国，章丽娜，徐晓旻，王骁，吴学珍，李纯兵，
申请(专利权)人：上海图博可特石油管道涂层有限公司，
类型：发明
国别省市：上海,31