功能高分子改性制备动物毛发复合纤维的方法及采用该方法制备的复合毛发纤维与织物技术

功能高分子改性制备动物毛发复合纤维的方法及采用该方法制备的复合毛发纤维与织物，其特征是所述方法由以下步骤组成：(1)原位吸附，将作为原料的动物毛发纤维充分浸泡在苯胺溶液中至苯胺在动物毛发纤维原位达到吸附平衡；(2)原位聚合，将掺杂酸加入到步骤(1)的浸泡体系中，调节苯胺溶液pH值为1～6，再将引发剂逐滴加入引发聚合。

Method for preparing animal hair composite fiber by functional polymer modification and composite hair fiber and fabric prepared by the method

Hair fiber composite functional polymer modified preparation of animal hair fiber and the preparation method and fabric, which is characterized in that the method comprises the following steps: (1) in situ adsorption, as animal hair fibers fully immersed in aniline solution to aniline in situ to animal hair fiber adsorption equilibrium; (2) in situ polymerization, doping acid is added to the step (1) immersion system, regulation of aniline solution pH value of 1 to 6, and then added dropwise polymerization initiator.

【技术实现步骤摘要】
功能高分子改性制备动物毛发复合纤维的方法及采用该方法制备的复合毛发纤维与织物
本专利技术涉及一种基于导电高分子材料的防静电复合动物毛发纤维及其制备方法。
技术介绍
羊毛是一种性能优异的动物毛发纤维，是纺织产品中应用最多的动物毛发纤维。具有优秀的保暖性、高吸水性、耐用性、耐洗性，并且毛质柔软、弹性好、不宜打皱，是衣服面料中最优秀的织物。同时具有优越的电气绝缘性能，但因其绝缘性好，易产生静电，此在日常工业生产及生活中也带来很多麻烦，甚至灾难。近些年来随着便携式电子产品的迅速发展，对织物的防静电和电磁屏蔽性能提出了更高的要求。因此改变羊毛材料的绝缘性，具有重要的现实意义。为了使常规的动物毛发纤维具有抗静电性，可以采用导电高分子材料来提高其导电性。与其他的导电高分子相比，聚苯胺具有单体原料易得到，合成工艺简单，掺杂现象独特，电导率较高，在空气中具有良好的稳定性等优点，是目前最有前途的导电高分子之一。但是因为聚苯胺分子链的共轭结构以及分子链间强烈的相互作用力导致该材料难于吸附到其他纤维材料上。中国专利申请CN201510483999.4公开了一种聚苯胺/涤纶复合纤维的制备技术，该工艺虽然可以得本文档来自技高网...

【技术保护点】
功能高分子改性制备动物毛发复合纤维的方法，其特征是所述方法由以下步骤组成：(1)原位吸附，将作为原料的动物毛发纤维充分浸泡在苯胺溶液中至苯胺在动物毛发纤维原位达到吸附平衡；(2)原位聚合，将掺杂酸加入到步骤(1)的浸泡体系中，调节苯胺溶液pH值为1～6，再将引发剂逐滴加入引发聚合。

【技术特征摘要】
1.功能高分子改性制备动物毛发复合纤维的方法，其特征是所述方法由以下步骤组成：(1)原位吸附，将作为原料的动物毛发纤维充分浸泡在苯胺溶液中至苯胺在动物毛发纤维原位达到吸附平衡；(2)原位聚合，将掺杂酸加入到步骤(1)的浸泡体系中，调节苯胺溶液pH值为1～6，再将引发剂逐滴加入引发聚合。2.如权利要求1所述的方法，其特征是所述引发剂为过硫酸铵、过硫酸钾、氯化铁、重铬酸钾、过氧化氢中的至少一种，苯胺与引发剂的物质的量比为优选为1:1。3.如权利要求2所述的方法，其特征是所述的引发剂逐滴加入的引发时间为0.5～2小时，引发剂加入后的聚合反应时间为2～36小时。4.如权利要求3的方法，其特征是所述的掺杂酸为盐酸、硫酸、硝酸、甲酸、乙酸、草...