The invention discloses a double N, N (three trimethylsilyl) allyl amine and preparation method thereof, relates to the field of organic polymer materials, the method comprises the following steps: when the temperature is less than 30 DEG C under the condition, according to the quality, the catalyst and 1 allylamine added to the reactor mixing and the catalyst Lewis acid into a reaction kettle; B, adding 1.1 ~ 1.3 copies of six methyl two silazane after heating to 90 to 110 DEG C, holding 4 ~ 6h N, N double (three trimethylsilyl) allyl amine crude. The invention can increase the yield and purity of the product, and can reduce the production cost, and is friendly to the equipment and the environment.
【技术实现步骤摘要】
一种N，N-双(三甲基甲硅烷基)烯丙基胺及其制备方法
本专利技术涉及有机高分子材料领域，具体涉及一种N，N-双(三甲基甲硅烷基)烯丙基胺及其制备方法。
技术介绍
聚酰亚胺(Polyimide，PI)是主链上含有酰亚胺环的一类聚合物，耐热性能和绝缘性能较好，广泛用于航空航天、电子电气等领域，同时也扩展至胶粘、过滤分离等领域，这些领域对聚酰亚胺的性能提出了更高的要求。为改良聚酰亚胺的性能，通常采用含氟单体参与反应，但是，含氟单体本身的价格比较昂贵，导致合成成本较高，为此，现已开发使用有机硅用于改性聚酰亚胺，使其具有较好溶解性、粘接性、耐高低温性和加工性，更低的吸湿率及更低的介电常数等。1966年Kuckertz首先合成了聚酰亚胺硅氧烷，之后，St.Clair等以同样的方法合成出热塑性聚酰亚胺硅氧烷，并成功地将它用作高强粘接剂和模塑料。含硅聚酰亚胺的研究表明，向聚酰亚胺的骨架中引入柔性硅氧烷嵌段后，由于硅氧烷链段优先向共聚物表面迁移，使共聚物具有更低吸水性和更高抗原子氧化性能，因此得到的聚酰亚胺具有较好加工性、耐热性、耐候性和机械性能。但是，为了使得聚酰亚胺的使用范围更...
【技术保护点】
一种N，N‑双(三甲基甲硅烷基)烯丙基胺的制备方法，其特征在于：包括以下步骤：A、在温度小于30℃的条件下，按质量份，将催化剂和1份烯丙胺加入反应釜中搅拌均匀，所述催化剂为路易斯酸；B、向反应釜中加入1.1～1.3份六甲基二硅氮烷后升温至90～110℃，保温4～6h得到N，N‑双(三甲基甲硅烷基)烯丙基胺粗品；所述反应机理为：
【技术特征摘要】
1.一种N，N-双(三甲基甲硅烷基)烯丙基胺的制备方法，其特征在于：包括以下步骤：A、在温度小于30℃的条件下，按质量份，将催化剂和1份烯丙胺加入反应釜中搅拌均匀，所述催化剂为路易斯酸；B、向反应釜中加入1.1～1.3份六甲基二硅氮烷后升温至90～110℃，保温4～6h得到N，N-双(三甲基甲硅烷基)烯丙基胺粗品；所述反应机理为：2.如权利要求1所述的一种N，N-双(三甲基甲硅烷基)烯丙基胺的制备方法，其特征在于：所述催化剂的用量为烯丙胺和六甲基二硅氮烷质量之和的2～4％。3.如权利要求1所述的一种N，N-双(三甲基甲硅烷基)烯丙基胺的制备方法，其特征在于：所述催化剂为三氟甲磺酸，浓硫酸，活性三氯化铝、四氯化钛中的至少一种。4.如权利要求1所述的一种N，N-双(三甲基甲硅烷基)烯丙基胺的制备方法，其特征在于：所述步骤A中的反应温度为-30～30℃。5.如权利要求4所述的一种N，N-双(三甲基甲硅烷基)烯丙...
【专利技术属性】
技术研发人员：冯琼华，肖俊平，梁成凯，王智威，
申请(专利权)人：湖北新蓝天新材料股份有限公司，
类型：发明
国别省市：湖北,42