The invention relates to the technical field of nano coatings, especially a flame retardant nano coating, in accordance with the mass fraction meter comprises the following components: 40-80 polyester resin, two formic acid and two phthalic ester 8-15, nano silica 3.4-5.6, polyethylene glycol 3-9, flame retardant 5-10, polyoxyethylene polyoxypropylene glycerol ether 1.8-2.5, ceramic fiber 12-18, barium sulfate 10-15, deionized water 45-60. Using the above formula, flame retardant nano coating of the invention, strengthen effective flame retardant effect, while reducing the resistance to impact of brittle materials, and greatly prolong the service life of material; in addition, effectively prevent material aging phenomenon.
【技术实现步骤摘要】
一种阻燃纳米涂料
本专利技术涉及纳米涂料
，特别是一种阻燃纳米涂料。
技术介绍
由于纳米微粒的小尺寸效应、表面效应、量子尺寸效应和宏观量子隧道效应等使得它们在磁、光、电、敏感等方面呈现常规材料不具备的特性。因此纳米微粒在磁性材料、电子材料、光学材料、高致密度材料的烧结、催化、传感、陶瓷增韧等方面有广阔的应用前景。一般来说，纳米涂料必须满足两个条件：首先，涂料中至少有一相的粒径尺寸在1—100nm的粒径范围；其次，纳米相的存在使涂料的性能要有明显的提高或具有新的功能。
技术实现思路
本专利技术需要解决的技术问题是提供一种阻燃纳米涂料。为解决上述的技术问题，本专利技术的一种阻燃纳米涂料，按照质量份数计包括以下组分：聚酯树脂40-80份，邻苯二甲酸二辛酯8-15份，纳米二氧化硅3.4-5.6份，聚乙二醇3-9份，阻燃剂5-10份，聚氧丙烯聚氧乙烯甘油醚1.8-2.5份，陶瓷纤维12-18份，硫酸钡10-15份，去离子水45-60份。进一步的，按照质量份数计包括以下组分：聚酯树脂40份，邻苯二甲酸二辛酯8份，纳米二氧化硅3.4份，聚乙二醇3份，阻燃剂5份，聚氧丙烯聚氧乙烯甘油醚1.8份，陶瓷纤维12份，硫酸钡10份，去离子水45份。进一步的，按照质量份数计包括以下组分：聚酯树脂80份，邻苯二甲酸二辛酯15份，纳米二氧化硅5.6份，聚乙二醇9份，阻燃剂10份，聚氧丙烯聚氧乙烯甘油醚2.5份，陶瓷纤维18份，硫酸钡15份，去离子水60份。进一步的，按照质量份数计包括以下组分：聚酯树脂55份，邻苯二甲酸二辛酯9份，纳米二氧化硅4.1份，聚乙二醇5份，阻燃剂6份，聚氧丙...
【技术保护点】
一种阻燃纳米涂料，其特征在于，按照质量份数计包括以下组分：聚酯树脂40‑80份，邻苯二甲酸二辛酯8‑15份，纳米二氧化硅3.4‑5.6份，聚乙二醇3‑9份，阻燃剂5‑10份，聚氧丙烯聚氧乙烯甘油醚1.8‑2.5份，陶瓷纤维12‑18份，硫酸钡10‑15份，去离子水45‑60份。
【技术特征摘要】
1.一种阻燃纳米涂料，其特征在于，按照质量份数计包括以下组分：聚酯树脂40-80份，邻苯二甲酸二辛酯8-15份，纳米二氧化硅3.4-5.6份，聚乙二醇3-9份，阻燃剂5-10份，聚氧丙烯聚氧乙烯甘油醚1.8-2.5份，陶瓷纤维12-18份，硫酸钡10-15份，去离子水45-60份。2.按照权利要求1所述的一种阻燃纳米涂料，其特征在于，按照质量份数计包括以下组分：聚酯树脂40份，邻苯二甲酸二辛酯8份，纳米二氧化硅3.4份，聚乙二醇3份，阻燃剂5份，聚氧丙烯聚氧乙烯甘油醚1.8份，陶瓷纤维12份，硫酸钡10份，去离子水45份。3.按照权利要求1所述的一种阻燃纳米涂料，其特征在于，按照质量份数计包括以下组分：聚酯树脂80份，邻苯二甲酸...