The invention discloses an anti void powder coating, which comprises the following components: quality polyester resin 50 70; 0.1 1.5 meteorological silica; 0.01 polyvinyl butyral 3; curing agent 3 8; 10 mica powder 20; titanium dioxide 10 25; leveling agent 0.5 1.5; 0.1 benzoin 1; 0 5 pigment. The weather and silica mixed with appropriate proportion of polyvinyl butyral quality, get the anti void special agent, powder coating increased melt viscosity or thixotropic effect, which is coated on the surface of workpiece and the corners of the powder in the spraying, and the cured film, like the plane position as uniform, no shrinkage, fertilizer the edge of the phenomenon, and the toughness was improved obviously.
【技术实现步骤摘要】
本专利技术涉及一种粉末涂料,具体涉及一种抗空隙粉末涂料。
技术介绍
粉末涂料是固体涂料,没有甲醛、苯类等有毒物质的排放,是三大环保涂料之一,应用非常广泛;而且使用便捷,使用率非常高,利用率超过90%。还有突出的综合性能,在各个行业上都有比较好的应用。粉末涂料以符合环保,出色的耐化学腐蚀性,机械强度高等性能,备受青睐。传统的粉末涂料因其自身的缺陷,固态熔融转台下流动性差,以及高压静电喷涂,在不规则工件的拐角和缝隙之间产生的磁场屏蔽效应,使得涂层部分过厚,边角部分喷涂不到,从而失去保护作用。
技术实现思路
为解决现有技术的不足,本专利技术的目的在于提供一种边角全覆盖、厚度均匀的抗空隙粉末涂料。为了实现上述目标,本专利技术采用如下的技术方案:一种抗空隙粉末涂料,包括以下质量份数的组分:聚酯树脂50-70份;气象二氧化硅0.1-1.5份;聚乙烯醇缩丁醛0.01-3份;固化剂3-8份;云母粉10-20份;钛白粉10-25份;流平剂0.5-1.5份;安息香0.1-1份;颜料0-5份。上述聚酯树脂的酸值为25-45mgKOH/g,软化点为100-200℃,玻璃化温度大于60℃。上述气象二氧化硅的白度≥93%,粒度D97um为4.0-6.5。上述聚乙烯醇缩丁醛为白色粉末,玻璃化温度为66-84℃。优选的,上述聚乙烯醇缩丁醛的质量份数为0.1-1.5。上述气象二氧化硅和聚乙烯醇缩丁醛的质量份数比为1:0.1-1:2。优选的,上述气象二氧化硅和聚乙烯醇缩丁醛的质量份数比为1:0.5。上述固化剂为三缩水异氰尿酸酯。上述固化剂与聚酯树脂的质量份数比为7:93-10:90。本专利技术 ...
【技术保护点】
一种抗空隙粉末涂料,其特征在于,包括以下质量份数的组分:聚酯树脂50‑70份;气象二氧化硅0.1‑1.5份;聚乙烯醇缩丁醛0.01‑3份;固化剂3‑8份;云母粉 10‑20份;钛白粉 10‑25份;流平剂0.5‑1.5份;安息香0.1‑1份;颜料0‑5份。
【技术特征摘要】
1.一种抗空隙粉末涂料,其特征在于,包括以下质量份数的组分:聚酯树脂50-70份;气象二氧化硅0.1-1.5份;聚乙烯醇缩丁醛0.01-3份;固化剂3-8份;云母粉10-20份;钛白粉10-25份;流平剂0.5-1.5份;安息香0.1-1份;颜料0-5份。2.根据权利要求1所述的一种抗空隙粉末涂料,其特征在于,所述聚酯树脂的酸值为25-45mgKOH/g,软化点为100-200℃,玻璃化温度大于60℃。3.根据权利要求1所述的一种抗空隙粉末涂料,其特征在于,所述气象二氧化硅的白度≥93%,粒度D97um为4.0-6.5。4.根据权利要求1所述的一种抗空隙粉末涂料,其特征在于,所述...
【专利技术属性】