The invention discloses a low frequency vibration compacting concrete, including cementitious material and mass of the cementitious materials from 1 to 2% of the additive, the additive consists of viscosity modifying agent, defoaming agent and water reducing agent, wherein the viscosity modifier dosage for 0.1% to cementitious materials the quality of 0.3%, the amount of defoaming agent and the mass of the cementitious materials from 0.01% to 0.05%, the remaining group was divided into water reducing agent. The invention comprehensively solves the difficult problems of difficult to be vibrated and compacted in the production process of prefabricated parts and the multiple pores defects on the surface after hardening, and greatly improves the quality of the components.
【技术实现步骤摘要】
一种低频振捣密实混凝土
本专利技术属于混凝土
，涉及一种低频振捣密实混凝土。
技术介绍
预制构件的生产，在成型阶段有振捣工艺，与振捣工艺相关的设备为振动台，振动台的振动模式有如下3种：(1)水平振动；(2)垂直振动：(3)混合振动。水平振动和垂直振动即为低频振动，混合振动为高频振动。低频振动噪音小，但是不易振捣密实；高频振动易于振捣密实，但是生产噪音大。装配式建筑是建筑发展的方向，预制构件厂将吸纳一大批的产业工人，预制构件厂的工作环境显得尤为重要，因而低频振捣密实混凝土具有重要的实用价值。预制装配式建筑的部品部件生产所需混凝土与预拌商品混凝土在配合比设计上基本一致，都遵循保罗米公式，所需原材料差异也较小，虽然如此，但结合预制装配式建筑部品部件的生产工艺，即尽早收光抹面，混凝土早期强度发展快，早期强度高，便于拆模起吊等，因此，该行业对混凝土的施工性能与预拌商品混凝土要求差异较大，通常，该行业配制的混凝土坍落度远低于预拌商品混凝土，例如，预制墙板等构件所用混凝土的坍落度通常在120—160mm，而泵送商品混凝土的坍落度一般大于180mm，甚至采用坍落度为250±...
【技术保护点】
一种低频振捣密实混凝土，其特征在于，包括：胶凝材料和占所述胶凝材料质量1.0～2.0％的外加剂，所述外加剂由粘度改性剂、消泡剂和减水剂组成，其中，所述粘度改性剂的用量占胶凝材料质量的0.1％～0.3％，所述消泡剂的用量占所述胶凝材料质量的0.01％～0.05％，剩余组分为减水剂。
【技术特征摘要】
1.一种低频振捣密实混凝土，其特征在于，包括：胶凝材料和占所述胶凝材料质量1.0～2.0％的外加剂，所述外加剂由粘度改性剂、消泡剂和减水剂组成，其中，所述粘度改性剂的用量占胶凝材料质量的0.1％～0.3％，所述消泡剂的用量占所述胶凝材料质量的0.01％～0.05％，剩余组分为减水剂。2.如权利要求1所述的低频振捣密实混凝土，其特征在于，所述胶凝材料包括水泥和活性掺合料；每立方米混凝土中，水泥用量为240～300kg，活性掺合料用量为60～120kg；每立方米混凝土中还包括如下用量的材料：砂920～1110kg，石810-1000kg和水160～175kg。3.如权利要求1所述的低频振捣密实混凝土，其特征在于，所述粘度改性剂为膨润土、黄原胶中的一种或两种，硫酸铝和硫酸亚...
【专利技术属性】
技术研发人员：叶浩文，李栋，周冲，尹述伟，
申请(专利权)人：中建科技有限公司，
类型：发明
国别省市：北京,11