The invention relates to a cold aerosol fire extinguishing agent, according to the weight percentage of raw materials including: solid ammonium polyphosphate 40~55%, ammonium sulfate 6~12%, talcum powder 3~8%, 10~15% silica, calcium carbonate 6~12%, sodium chloride 1~3%, magnesium stearate 6~12%, amino acid and inorganic acid salt 0.3~1.5%. The cold air sol fire extinguishing agent is prepared by mixing the said raw materials. The flame is not after the fire again, suitable for space and open space relatively sealed, compared to ordinary dry powder extinguishing ability is 10~12 times, can burst of class B, class C fire and A/B mixed fire, and does not destroy the ozone layer, has the advantages of environmental protection.
【技术实现步骤摘要】
冷气溶胶灭火剂
本专利技术属于消防
,具体涉及一种冷气溶胶灭火剂。
技术介绍
气溶胶灭火剂可分为热气溶胶和冷气溶胶。热气溶胶灭火剂是由氧化剂、还原剂、粘合剂、燃速调节剂等物质构成的固体混合剂,在电流或热引发下,经过药剂自身的氧化还原燃烧反应生成灭火用气溶胶,通过物理或化学降温的方法达到灭火目的。冷气溶胶灭火剂是利用机械或高压气体将固体或液体超细灭火微粒分散于气体中而形成的灭火溶剂。冷气溶胶灭火剂相当于普通灭火剂具有不附带二次危害的优点,开始被消防行业逐渐研究和推广。
技术实现思路
本专利技术目的是提供一种冷气溶胶灭火剂,环保,防止复燃、适用于相对密封的空间及开放空间,灭火效率更高。为了实现以上目的,本专利技术采用的技术方案为:一种冷气溶胶灭火剂,按照重量百分比的原料包括:固体聚磷酸铵40~55%,硫酸铵6~12%,滑石粉3~8%,二氧化硅10~15%,碳酸钙6~12%,氯化钠1~3%,硬脂酸镁6~12%,氨基酸无机酸盐0.3~1.5%。优选的,所述的冷气溶胶灭火剂,按照重量百分比的原料包括:固体聚磷酸铵50%,硫酸铵10%,滑石粉5%,二氧化硅12%,碳酸钙10%,氯化钠2%,硬脂酸镁10%,氨基酸无机酸盐1%。进一步的,所述的固体聚磷酸铵、硫酸铵、滑石、二氧化硅、碳酸钙、氯化钠、硬脂酸镁、氨基酸无机酸盐均为颗粒,且粒径为0.5μm~1μm。本专利技术的技术效果在于:将上述原料混合均匀,制得冷气溶胶灭火剂。灭火后火焰不会复燃,适用于相对密封的空间及开放空间,相比普通干粉其灭火能力是其10~12倍,能破灭B类、C类火灾和A/B类混合火灾,且其不破坏大气臭氧 ...
【技术保护点】
一种冷气溶胶灭火剂,其特征在于,按照重量百分比的原料包括:固体聚磷酸铵40~55%,硫酸铵6~12%,滑石粉3~8%,二氧化硅10~15%,碳酸钙6~12%,氯化钠1~3%,硬脂酸镁6~12%,氨基酸无机酸盐0.3~1.5%。
【技术特征摘要】
1.一种冷气溶胶灭火剂,其特征在于,按照重量百分比的原料包括:固体聚磷酸铵40~55%,硫酸铵6~12%,滑石粉3~8%,二氧化硅10~15%,碳酸钙6~12%,氯化钠1~3%,硬脂酸镁6~12%,氨基酸无机酸盐0.3~1.5%。2.根据权利要求1所述的冷气溶胶灭火剂,其特征在于,按照重量百分比的原料包...
【专利技术属性】
技术研发人员:桂永林,
申请(专利权)人:安徽新盾消防设备有限公司,
类型:发明
国别省市:安徽,34