The invention discloses a processing technology of functional fibers, comprises the following steps: step one, adding tourmaline powder, in fiber pulping and stirring, adding amount of tourmaline powder is 18 ~ 22g/ square meters; step two, stir in the fiber pulp and tourmaline powder into graphene, stirring, adding the amount of graphene is 1m g/ square meters; step three, step two in the fiber with the mixture of metal complex mixing machine, the formation of functional fiber, adding metal complexes for 10 machine g/ square meters, weaving process by the fiber is also included, made by the process with cloth sent to the far infrared, release negative ions, with magnetotherapy effect and antibacterial function, good toughness and strength and the fiber has high tensile, good performance, durable Use, use health.
【技术实现步骤摘要】
本专利技术涉及一种纺织领域,尤其涉及一种功能性纤维的加工工艺,还涉及利用该纤维进行织布的工艺。
技术介绍
随着人们生活质量的提高,功能纤维及纺织品的发展逐渐受到人们的关注和喜爱,功能纤维是指除一般纤维具有的物理机械性能外,还具有某种特殊功能的新型纤维。如具有防水、防油、防污功能的“三防”纤维,其织物将具有一定的防水、防污或拒油等功能,可以减少服装的洗涤次数、又能降低洗衣劳动强度。上述功能的布料主要是功能整理剂的作用,功能整理剂作为生产功能纤维的主要助剂,其应用也越来越广。研究发现,含氟聚合物整理剂不仅具有防水、防油、防污等特性外,还具有良好的化学稳定性和热稳定性,常用于织物的后整理工序,经其整理的织物穿着舒适,并显示与一般烃类或有机硅防水剂不具备的防油和防污性能,已成为当今防水剂的研究的热点。但是衣物如果不经常清洗,往往会产生大量的细菌,不利于人们身体健康,因此如果生产抗菌性纤维成为目前需要解决的技术问题之一。
技术实现思路
本专利技术所要解决的技术问题是提供一种具有磁疗、抗菌作用的功能性纤维的加工工艺。为解决上述技术问题,本专利技术的技术方案是:一种功能性纤维的加工工艺,包括以下步骤,步骤一、在纤维制浆中加入电气石粉末,搅拌均匀,电气石粉末的加入量为18~22g/平方米;步骤二、在搅拌均匀的纤维制浆与电气石粉末加入石墨烯,搅拌均匀,石墨烯的加入量为0.8~1.2mg/平方米;步骤三、在步骤二的纤维混合物中加入机金属络合物,搅拌均匀,形成功能纤维,机金属络合物的加入量为8~12g/平方米。本专利技术还涉及一种利用上述功能性纤维进行织布的工艺,包括以下步骤,步 ...
【技术保护点】
一种功能性纤维的加工工艺,其特征在于:包括以下步骤,步骤一、在纤维制浆中加入电气石粉末,搅拌均匀,电气石粉末的加入量为18~22g/平方米;步骤二、在搅拌均匀的纤维制浆与电气石粉末加入石墨烯,搅拌均匀,石墨烯的加入量为0.8~1.2m g/平方米;步骤三、在步骤二的纤维混合物中加入机金属络合物,搅拌均匀,形成功能纤维,机金属络合物的加入量为8~12 g/平方米。
【技术特征摘要】
1.一种功能性纤维的加工工艺,其特征在于:包括以下步骤,步骤一、在纤维制浆中加入电气石粉末,搅拌均匀,电气石粉末的加入量为18~22g/平方米;步骤二、在搅拌均匀的纤维制浆与电气石粉末加入石墨烯,搅拌均匀,石墨烯的加入量为0.8~1.2mg/平方米;步骤三、在步骤二的纤维混合物中加入机金属络合物,搅拌均匀,形成功能纤维,机金属络合物的加入...