The present invention relates to the technical field of cardboard production, in particular to a method of producing high strength paper board, (1) ingredients: according to the weight weighed raw materials, mineral fiber 10 15 copies, 10 copies of the 5 glass fiber, carbon fiber 3 dispersant 1 5 copies, 2 copies, retention agent 0.5 0.8 copies, the raw materials are mixed uniformly into a composite agent; (2) pulping, the composite agent is added in the ordinary pulp pulping machine, mixing evenly, prepared paper pulp; (3) making use of base paper, papermaking equipment base paper pulp paper; (4) making use of corrugated cardboard. Paper production line and adhesive paper will produce high strength of paperboard. The invention discloses a method for producing a high strength box board paper, which has the advantages of large strength of the box board paper, bending not easily during use and strong tearing resistance.
【技术实现步骤摘要】
本专利技术涉及纸板生产
，尤其是一种高强度箱板纸的生产方法。
技术介绍
现有技术中箱板纸的强度都比较低，在使用过程中当纸箱上方存在重压的情况下，容易出现弯折、撕裂的情况。
技术实现思路
本专利技术的目的是为了解决上述技术的不足而提供一种高强度箱板纸的生产方法，其生产的箱板纸制作成纸箱强度高，使用寿命长。为了达到上述目的，本专利技术所设计的一种高强度箱板纸的生产方法，（1）配料：按重量份数称取原料，矿物纤维10-15份，玻璃纤维5-10份，碳纤维3-5份，分散剂1-2份，助留剂0.5-0.8份，将上述原料混合均匀制成复合剂；（2）制浆，将上述复合剂加入制浆机中的普通纸浆中，搅拌均匀，制得原纸纸浆；（3）制作原纸，利用造纸设备将原纸纸浆制成原纸；（4）制作纸板，利用瓦楞纸生产线及粘胶剂将原纸制作成高强度箱板纸。本专利技术所得到的一种高强度箱板纸的生产方法，其生产的箱板纸强度大，使用过程中不易发生弯折，抗撕裂能力强。具体实施方式下面通过实施例对本专利技术作进一步的描述。实施例1：本实施例描述的一种高强度箱板纸的生产方法，（1）配料：按重量份数称取原料，矿物纤维10份，玻璃纤维5份，碳纤维3份，分散剂1份，助留剂0.5份，将上述原料混合均匀制成复合剂；（2）制浆，将上述复合剂加入制浆机中的普通纸浆中，搅拌均匀，制得原纸纸浆；（3）制作原纸，利用造纸设备将原纸纸浆制成原纸；（4）制作纸板，利用瓦楞纸生产线及粘胶剂将原纸制作成高强度箱板纸。实施例2：本实施例描述的一种高强度箱板纸的生产方法，（1）配料：按重量份数称取原料，矿物纤维15份，玻璃纤维10份，碳纤维5份...
【技术保护点】
一种高强度箱板纸的生产方法，其特征是：（1）配料：按重量份数称取原料，矿物纤维10‑15份，玻璃纤维5‑10份，碳纤维3‑5份，分散剂1‑2份，助留剂0.5‑0.8份，将上述原料混合均匀制成复合剂；（2）制浆，将上述复合剂加入制浆机中的普通纸浆中，搅拌均匀，制得原纸纸浆；（3）制作原纸，利用造纸设备将原纸纸浆制成原纸；（4）制作纸板，利用瓦楞纸生产线及粘胶剂将原纸制作成高强度箱板纸。
【技术特征摘要】
1.一种高强度箱板纸的生产方法，其特征是：（1）配料：按重量份数称取原料，矿物纤维10-15份，玻璃纤维5-10份，碳纤维3-5份，分散剂1-2份，助留剂0.5-0.8份，将上述原料混合均匀制成...