The present invention relates to the technical field of paint, especially a waterproof coating, the water-proof coating quality parts are as follows: vinyl acetate acrylate copolymer emulsion 10 30 copies, 12 copies, 6 pure acrylic zinc powder 1.2 2.5 copies, 13 copies of the 8 styrene acrylic emulsion and graphite powder 10, 8 hydroxyl 6 ethyl cellulose 10, nitro magnetic white water 8, 4 TiO2 2.4 4.8 copies, 1.8 copies of antioxidant 0.8. The beneficial effect of the technical scheme of the invention is that the invention can effectively prolong paint water yellowing, mildew, easy to fall off in time, and the use of other ingredients, to further improve the coating resistance to new energy, but also improve the coating corrosion resistance, crack resistance, and waterproof coating of the invention also has environmental protection, no smell and other advantages.
【技术实现步骤摘要】
本专利技术涉及涂料
，尤其是一种耐水涂料。
技术介绍
涂料涂于物体表面能形成具有保护、装饰或特殊性能（如绝缘、防腐、标志等）的固态涂膜的一类液体或固体材料的总称。包括油漆、水性漆、木器漆、粉末涂料、木蜡油。不好的涂料在遇水干后，容易干裂，表面出现鳞片状脱落，使家装后容易返工，给用户带来难以弥补的损失，而且涂料制作原料成本较高，无法满足用户经济效益。
技术实现思路
本专利技术的目的是：克服现有技术中的不足，提供一种遇水后不易脱落、变黄，原料配比合理，成本低的耐水涂料。为解决上述技术问题，本专利技术采用的技术方案如下：一种耐水涂料，所述耐水涂料的质量份组成如下：醋酸乙烯-丙烯酸共聚乳液10-30份、纯丙烯酸6-12份、锌粉1.2-2.5份、苯丙乳液8-13份、石墨粉8-10份、羟乙基纤维素6-10份、硝基磁化白水4-8份、二氧化钛2.4-4.8份、抗氧剂0.8-1.8份。进一步的，所述醋酸乙烯-丙烯酸共聚乳液选用高聚物为15-20份。进一步的，所述的纯丙烯酸为8-10份。进一步的，所述的苯丙乳液为10份。进一步的，所述的硝基磁化白水5份。采用本专利技术的技术方案的有益效果是：本专利技术能有效延长涂料遇水变黄、发霉、易脱落的时间，与其他成分配伍使用，进一步提高了涂料的耐水新能，同时也提高了涂料的耐腐蚀性，抗裂性，而且，本专利技术的耐水涂料还具有环保、无刺激性气味等优势。具体实施方式下面结合具体实施例对本专利技术做进一步说明。实施例1一种耐水涂料，所述耐水涂料的质量份组成如下：醋酸乙烯-丙烯酸共聚乳液10-30份、纯丙烯酸6-12份、锌粉1.2-2.5份、苯丙...
【技术保护点】
一种耐水涂料，其特征在于，所述耐水涂料的质量份组成如下：醋酸乙烯‑丙烯酸共聚乳液10‑30份、纯丙烯酸6‑12份、锌粉1.2‑2.5份、苯丙乳液8‑13份、石墨粉8‑10份、羟乙基纤维素6‑10份、硝基磁化白水4‑8份、二氧化钛2.4‑4.8份、抗氧剂0.8‑1.8份。
【技术特征摘要】
1.一种耐水涂料，其特征在于，所述耐水涂料的质量份组成如下：醋酸乙烯-丙烯酸共聚乳液10-30份、纯丙烯酸6-12份、锌粉1.2-2.5份、苯丙乳液8-13份、石墨粉8-10份、羟乙基纤维素6-10份、硝基磁化白水4-8份、二氧化钛2.4-4.8份、抗氧剂0.8-1.8份。2.根据权利要求1所述的一种...