The invention relates to a new type of high temperature resistant conductive grease, including base oil, graphene, carbon black, Zinc Oxide, stearic acid, graphite fluoride, overbased calcium sulfonate, two ethyl phosphite, polysulfide, mass fraction of each component is 80 base oil 100, 2, 1 graphene carbon black 5 8, Zinc Oxide 8 16, stearic acid 10 15, 16, 10 graphite fluoride overbased calcium sulfonate 5 10 phosphite two ethyl 6, 5 polysulfide 5 9. The novel high temperature conductive lubricating paste adopts advanced biological technology and is used for rolling a high performance grease on a rolling component, containing special polymer, and having excellent high temperature property. Applicable to high speed gear box, high temperature resistance, high viscosity, easy running oil, durable and efficient.
【技术实现步骤摘要】
一种新型耐高温导电润滑膏
本专利技术涉及一种润滑材料，具体地讲，本专利技术涉及一种新型耐高温导电润滑膏。
技术介绍
润滑脂是为了解决设备在运转时产生离心力的状态下，为减少设备摩擦磨损需要的一种润滑材料。与润滑油相比，由于使用更加容易的原因，被更广泛的应用于润滑各类产业机械的润滑部分。目前的普遍现象是用国产高温脂使用，频繁停机、注油，影响正常生产，浪费能源，污染环境，劳动强度大，设备养护成本高。一部分企业用进口产品（例如美国LE公司的1275脂），价格昂贵，运输周期长，成本费用高。
技术实现思路
针对现有技术中存在的上述不足，本专利技术所要解决的技术问题是提供一种保养效果好的新型耐高温导电润滑膏。本专利技术解决其技术问题所采用的技术方案是：提供一种新型耐高温导电润滑膏，包括基础油、石墨烯、碳黑、氧化锌、硬脂酸、氟化石墨、高碱值磺酸钙、亚磷酸二乙酯、聚硫化物，各组分的质量份数为：基础油80-100、石墨烯1-2、碳黑5-8、氧化锌8-16、硬脂酸10-15、氟化石墨10-16、高碱值磺酸钙5-10、亚磷酸二乙酯5-6、聚硫化物5-9。作为优选，所述新型耐高温导电润滑膏还包...
【技术保护点】
一种新型耐高温导电润滑膏，其特征在于：包括基础油、石墨烯、碳黑、氧化锌、硬脂酸、氟化石墨、高碱值磺酸钙、亚磷酸二乙酯、聚硫化物，各组分的质量份数为：基础油80‑100、石墨烯1‑2、碳黑5‑8、氧化锌8‑16、硬脂酸10‑15、氟化石墨10‑16、高碱值磺酸钙5‑10、亚磷酸二乙酯5‑6、聚硫化物5‑9。
【技术特征摘要】
1.一种新型耐高温导电润滑膏，其特征在于：包括基础油、石墨烯、碳黑、氧化锌、硬脂酸、氟化石墨、高碱值磺酸钙、亚磷酸二乙酯、聚硫化物，各组分的质量份数为：基础油80-100、石墨烯1-2、碳黑5-8、氧化锌8-16、硬脂酸10-15、氟化石墨10-16、高碱值磺酸钙5-10、亚磷酸二乙酯5-6、聚硫化物5-9。2.根据权利要求1所述的新型耐高温导电润滑膏，其特征在于：所述新型耐高温导电润滑膏还包括基础油100、石墨烯1、碳黑7、氧化锌12、硬脂酸10、氟化石墨11、高碱值磺酸钙9、亚磷酸二乙酯6、聚硫化物7。3.根据权利要求2所述的新型耐高温导电润滑膏，其特征在于：所述基础油选自合成烃、合成酯、聚醚、硅油、含氟油、磷酸酯中的一种或任意几种的混合物，所述基础油的50℃运动粘度范围在500cst～15...